This study aims at finding appropriate adhesive conditions with special regard the material of 'fusible padding cloth inter ling' was frequently used for leather. As for leather material, pig suede, sheep suede were selected and drum dyed, cow split, napa have also been used. Mixed spinning non-wove...
This study aims at finding appropriate adhesive conditions with special regard the material of 'fusible padding cloth inter ling' was frequently used for leather. As for leather material, pig suede, sheep suede were selected and drum dyed, cow split, napa have also been used. Mixed spinning non-woven fabric (polyester $50\%$, nylon $50\%$) were used as for padding cloth. Experimental appearance has been observed under the following adhesive conditions: Temperature of press were devided four levers; $120^{\circ}C$, $130^{\circ}C$, $140^{\circ}C$, $150^{\circ}C$, respectively. Adhesive time has been limited 5, 10, 15 second each. And the pressure has been conditioned as $0.2kg/cm^2$ continuously. After all this experiment, it was discovered that the material which had long contact with low temperature conditions has similar adhesive power to material that has short contact with high temperature conditions. There is a great difference according to the leather's dying process, the finishing method of the cloth, and the part of leather surface. The best condition for suede are $140^{\circ}C$, $150^{\circ}C$, at 10 seconds. and for D/D, NAPA, $130^{\circ}C$, at 10 seconds. Although the conditions of $150^{\circ}C$, at 15 seconds was possible for split, the process time can be shortened according to the increase of temperature.
This study aims at finding appropriate adhesive conditions with special regard the material of 'fusible padding cloth inter ling' was frequently used for leather. As for leather material, pig suede, sheep suede were selected and drum dyed, cow split, napa have also been used. Mixed spinning non-woven fabric (polyester $50\%$, nylon $50\%$) were used as for padding cloth. Experimental appearance has been observed under the following adhesive conditions: Temperature of press were devided four levers; $120^{\circ}C$, $130^{\circ}C$, $140^{\circ}C$, $150^{\circ}C$, respectively. Adhesive time has been limited 5, 10, 15 second each. And the pressure has been conditioned as $0.2kg/cm^2$ continuously. After all this experiment, it was discovered that the material which had long contact with low temperature conditions has similar adhesive power to material that has short contact with high temperature conditions. There is a great difference according to the leather's dying process, the finishing method of the cloth, and the part of leather surface. The best condition for suede are $140^{\circ}C$, $150^{\circ}C$, at 10 seconds. and for D/D, NAPA, $130^{\circ}C$, at 10 seconds. Although the conditions of $150^{\circ}C$, at 15 seconds was possible for split, the process time can be shortened according to the increase of temperature.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.