The influence of builders on calcium deposition on the fabric was studied by laundering the cotton fabric with sodium carbonate, sodium metasilicate, sodium tripolyphosphate and built detergents in hard water. The laundry variables were: 1) Washing cycles: 5, 10, 20, 30 and 40 cycles. 2) Water hardn...
The influence of builders on calcium deposition on the fabric was studied by laundering the cotton fabric with sodium carbonate, sodium metasilicate, sodium tripolyphosphate and built detergents in hard water. The laundry variables were: 1) Washing cycles: 5, 10, 20, 30 and 40 cycles. 2) Water hardness: 100 ppm, 150 ppm, 200 ppm and 300 ppm. 3) Builders: $Na_2\;CO_3,\;Na_2\;SiO_3$ and STPP. 4) Detergents: Na-DBS, $Na-DBS+Na_2CO_3,\;Na-DBS+Na_2\;SiO_3,\;Na-DBS+STPP,\;Na-DBS+Na_2\;CO_3+STPP$, and $Na-DBS+Na_2\;SiO_3+STPP$. The fabric was washed for 15 minutes at 23+$1^{\circ}C$ in a washing machine(Gold Star WP 3007) under the similar condition with those of home laundering, and rinsed 3 times in the same water hardness for 5 minutes. The calcium deposits on the fabric was determined by EDTA-BACK titration methods. The results of this study were as follows: 1) The amount of calcium deposits on the fabric was increased with increasing wash cycles. This deposit was due to the build up of insoluble calcium carbonate. 2) As the water hardness increased, the amount of calcium deposits on the fabric was increased. 3) Alkaline builders, such as, $Na_2CO_3$ and $Na_2SiO_3$, promoted calcium deposition on the fabric, however STPP prevented calcium deposition on the fabric. 4) Fabric laundered with $Na-DBS+Na_2CO_3$ showed the highest calcium deposits on the fabric, and decreased with the order of $Na_2CO_3$, $Na-DBS+Na_2SiO_3$, and Na-DBS. And fabrics washed with phosphate-built detergents showed a small amount of calcium deposition.
The influence of builders on calcium deposition on the fabric was studied by laundering the cotton fabric with sodium carbonate, sodium metasilicate, sodium tripolyphosphate and built detergents in hard water. The laundry variables were: 1) Washing cycles: 5, 10, 20, 30 and 40 cycles. 2) Water hardness: 100 ppm, 150 ppm, 200 ppm and 300 ppm. 3) Builders: $Na_2\;CO_3,\;Na_2\;SiO_3$ and STPP. 4) Detergents: Na-DBS, $Na-DBS+Na_2CO_3,\;Na-DBS+Na_2\;SiO_3,\;Na-DBS+STPP,\;Na-DBS+Na_2\;CO_3+STPP$, and $Na-DBS+Na_2\;SiO_3+STPP$. The fabric was washed for 15 minutes at 23+$1^{\circ}C$ in a washing machine(Gold Star WP 3007) under the similar condition with those of home laundering, and rinsed 3 times in the same water hardness for 5 minutes. The calcium deposits on the fabric was determined by EDTA-BACK titration methods. The results of this study were as follows: 1) The amount of calcium deposits on the fabric was increased with increasing wash cycles. This deposit was due to the build up of insoluble calcium carbonate. 2) As the water hardness increased, the amount of calcium deposits on the fabric was increased. 3) Alkaline builders, such as, $Na_2CO_3$ and $Na_2SiO_3$, promoted calcium deposition on the fabric, however STPP prevented calcium deposition on the fabric. 4) Fabric laundered with $Na-DBS+Na_2CO_3$ showed the highest calcium deposits on the fabric, and decreased with the order of $Na_2CO_3$, $Na-DBS+Na_2SiO_3$, and Na-DBS. And fabrics washed with phosphate-built detergents showed a small amount of calcium deposition.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.