$\require{mediawiki-texvc}$
  • 검색어에 아래의 연산자를 사용하시면 더 정확한 검색결과를 얻을 수 있습니다.
  • 검색연산자
검색연산자 기능 검색시 예
() 우선순위가 가장 높은 연산자 예1) (나노 (기계 | machine))
공백 두 개의 검색어(식)을 모두 포함하고 있는 문서 검색 예1) (나노 기계)
예2) 나노 장영실
| 두 개의 검색어(식) 중 하나 이상 포함하고 있는 문서 검색 예1) (줄기세포 | 면역)
예2) 줄기세포 | 장영실
! NOT 이후에 있는 검색어가 포함된 문서는 제외 예1) (황금 !백금)
예2) !image
* 검색어의 *란에 0개 이상의 임의의 문자가 포함된 문서 검색 예) semi*
"" 따옴표 내의 구문과 완전히 일치하는 문서만 검색 예) "Transform and Quantization"
쳇봇 이모티콘
안녕하세요!
ScienceON 챗봇입니다.
궁금한 것은 저에게 물어봐주세요.

논문 상세정보

Glycerol 후처리에 의한 Free-formaldehyde 발생 억제 효과

The Effects of Glycerol Aftertreatment for Low-Formaldehyde Finishing

Abstract

To control the amounts of formaldehyde released from the cotton fabric finished with N-methylol compounds, glycerol was used as a formaldehyde-scavenging agent. It was observed the effects of catalysts and curing conditions when aftertreated with glycerol on melamine resin finished fabric. The effects of Different processes of glycerol treatment, and different resins, urea resin and melamine resin, were compared. The conclusions obtained from the results are as follows: 1) It was shown hatt the aftertreatment with glycerol (treated without catalyst) was more effective than treated with catalysts in controlling free formaldehyde. 2) The optimum curing temperature and curing time for the glycerol aftertreatment without adversely affecting the other properties of fabric was about $160^{\circ}C$, 3 min. 3) According to the increase of glycerol concentration in both aftertreatment and simultaneous treatment the amounts of free formaldehyde was reduced. The rate of decrease was manifest within the limits of $6\%$ in the case of simultaneous treatment with glycerol ana resins, and $3\%$ in the case of glycerol aftertreatment on resin finished fabrics. 4) Dry wrinkle recovery angle was decreased the increase of glycerol concentration. Melamine resin had a little adverse effect than urea resin, particulary glycerol aftertreatment. 5) The breaking strength was increased with the increase of glycerol concentration.

저자의 다른 논문

참고문헌 (0)

  1. 이 논문의 참고문헌 없음

이 논문을 인용한 문헌 (0)

  1. 이 논문을 인용한 문헌 없음

원문보기

원문 PDF 다운로드

  • ScienceON :

원문 URL 링크

원문 PDF 파일 및 링크정보가 존재하지 않을 경우 KISTI DDS 시스템에서 제공하는 원문복사서비스를 사용할 수 있습니다. (원문복사서비스 안내 바로 가기)

상세조회 0건 원문조회 0건

DOI 인용 스타일