The sintering properties of hydroxyapatite isolated from tuna bone and hydroxyapatite-containing wollastonite sintered by solid-state reaction was investigated. As the sinterability of hydroxyapatite dependent upon the particle size by dry milling, it showed a sintering. But the hydroxyapatite-conta...

The sintering properties of hydroxyapatite isolated from tuna bone and hydroxyapatite-containing wollastonite sintered by solid-state reaction was investigated. As the sinterability of hydroxyapatite dependent upon the particle size by dry milling, it showed a sintering. But the hydroxyapatite-containing wollastonite was appeared good sinterability. On X-ray measurements, the major phases of hydroxyapatite-containing wollastonite by solid state reaction at $1250^{\circ}C$ were identified as hydroxyapatite and pseudowollastonite(${\alpha}-CaSiO_3$). And the phases appeared as whitlockite [$Ca_3(PO_4)_2$] by decomposition of hydroxyapatite at higher temperature above $1250^{\circ}C$. The shapes of microstructure on SEM images changed from porous to dense bulk by elevating temperature. The mean bending strength of hydroxyapatite-containing wollastonite sintered by solid-state reaction at $1300^{\circ}C$ was about 18 MPa, it was close to the cancellous bone's maximum strength, 20 MPa.