$\require{mediawiki-texvc}$
  • 검색어에 아래의 연산자를 사용하시면 더 정확한 검색결과를 얻을 수 있습니다.
  • 검색연산자
검색연산자 기능 검색시 예
() 우선순위가 가장 높은 연산자 예1) (나노 (기계 | machine))
공백 두 개의 검색어(식)을 모두 포함하고 있는 문서 검색 예1) (나노 기계)
예2) 나노 장영실
| 두 개의 검색어(식) 중 하나 이상 포함하고 있는 문서 검색 예1) (줄기세포 | 면역)
예2) 줄기세포 | 장영실
! NOT 이후에 있는 검색어가 포함된 문서는 제외 예1) (황금 !백금)
예2) !image
* 검색어의 *란에 0개 이상의 임의의 문자가 포함된 문서 검색 예) semi*
"" 따옴표 내의 구문과 완전히 일치하는 문서만 검색 예) "Transform and Quantization"
쳇봇 이모티콘
안녕하세요!
ScienceON 챗봇입니다.
궁금한 것은 저에게 물어봐주세요.

논문 상세정보

시효처리와 thermal cycling이 치관전장용 복합레진의 2축굽힘강도에 미치는 영향

EFFECTS OF AGING AND THERMAL CYCLING ON THE BIAXIAL FLEXURE STRENGTH OF VENEERING RESIN COMPOSITES FOR CROWN

Abstract

This study was performed to evaluate the effect of aging and thermal cycling on the biaxial flexure strength of low commercially available veneering resin composites for crown(Dentacolor : DC, Artglass : AG, Esternia : ET and Targis : TG). Disc specimens were fabricated in a teflon mold giving 12mm in diameter and 1mm in thickness. All samples were divided into 4 groups. Group 1 was dried in a dessicator at $25^{\circ}C$ for 30 days. Group 2 was immersed in distilled water at $37^{\circ}C$ for 30 days. Group 3 was immersed in distilled water at $65^{\circ}C$ for 30 days. Group 4 was subjected to 10,000 thermal cycles between $5^{\circ}C\;and\;55^{\circ}C$, and the immersion time in each bath was 15 seconds per cycle. Biaxial flexure test was conducted using the ball-on-three-ball method at the cross head speed of 0.5mm/min and fracture surfaces were observed with scanning electoron microscope. The results obtained were summarized as follows; 1. Weibull modulus values, except for the AG group, decreased after thermal cycling treatment. 2. Biaxial flexure strength values of aging group at $37^{\circ}C$ were the lowest in all sample groups. Except for the DC group, strength values were significantly decreased for the drying group. 3. After thermal cycling test, the highest value of biaxial flexure strength of 188.8 MPa was observed in the ET group and the lowest value of 73.2 MPa was observed in the DC group. The strength values showed the significant differences in each group (p<0.05). 4. Observation of surfaces after thermal cycling test revealed the ditching in the part of surrounding large fillers.

참고문헌 (0)

  1. 이 논문의 참고문헌 없음

이 논문을 인용한 문헌 (0)

  1. 이 논문을 인용한 문헌 없음

원문보기

원문 PDF 다운로드

  • ScienceON :

원문 URL 링크

원문 PDF 파일 및 링크정보가 존재하지 않을 경우 KISTI DDS 시스템에서 제공하는 원문복사서비스를 사용할 수 있습니다. (원문복사서비스 안내 바로 가기)

상세조회 0건 원문조회 0건

DOI 인용 스타일