BaTiO$_3$ fine powders were synthesized by hydrothermal process from peroxo-coprecipitate precursors. The peroxo-coprecipitates were obtained by addition of the BaCl$_2$, TiCl$_4$, and $H_2O$$_2$ aqueous solution to an ammonium solution. Hydroth...

BaTiO$_3$ fine powders were synthesized by hydrothermal process from peroxo-coprecipitate precursors. The peroxo-coprecipitates were obtained by addition of the BaCl$_2$, TiCl$_4$, and $H_2O$$_2$ aqueous solution to an ammonium solution. Hydrothermal reaction was conducted at various reaction temperatures, times and pH ranges. Unlike the conventional hydrothermal synthesis which needs highly alkaline condition over pH 13 with KOH or NaOH, the present method offered well-developed crystalline (perovskite) BaTiO$_3$ powders synthesized below pH 12 with use of ammonium solution. It was found that the phase-pure fine powders were formed at temperatures as low as 11$0^{\circ}C$ and the properties of the powders synthesized over 13$0^{\circ}C$ were almost same regardless of the reaction time. BET surface area of the prepared powder was as high as 76 $m^2$/g and the calculated particle (particulate) size was below 20 nm. The ultrafine particulates formed weak agglomerates. The microstructure and dielectric properties of BaTiO$_3$ ceramics sintered at the temperature range of 1150~125$0^{\circ}C$ were evaluated.

주제어