NTIS 바로가기목재공학 = Journal of the Korean wood science and technology, v.50 no.3, 2022년, pp.167 - 178
SONG, Dabin (Wood Engineering Division, Department of Forest Products and Industry, National Institute of Forest Science) , KIM, Keonho (Wood Engineering Division, Department of Forest Products and Industry, National Institute of Forest Science)
To investigate the influence of manufacturing environment on bonding performance of mixed cross laminated wood (CLT) using polyurethane (PUR) adhesive, a boiling water soak delamination test according to the temperature and relative humidity was conducted. The 5-ply mixed CLT consisted of Japanese L...
ANSI, APA. 2018 Standard for Performance-Rated Cross-Laminated Timber (PRG 320). APA-The Engineered Wood Association, Tacoma, WA, USA.
Brandner, R., Flatscher, G., Ringhofer, A., Schickhofer, G., Thiel, A. 2016. Cross laminated timber (CLT): Overview and development. European Journal of Wood and Wood Products 74(3): 331-351.
Galvez, P., Armentia, S.L., Abenojar, J., Martinez, M.A. 2020. Effect of moisture and temperature on thermal and mechanical properties of structural polyurethane adhesive joints. Composite Structures 247: 112443.
Gong, Y., Wu, G., Ren, H. 2016. Block shear strength and delamination of cross-laminated timber fabricated with Japanese larch. BioResources 11(4): 10240-10250.
Han, Y., Park, Y., Yang, S.Y., Chung, H., Chang, Y.S., Yeo, H. 2019. Dimensional changes of cross-laminated specimens produced under different conditions due to humidity variation. BioResources 14(2): 4035-4046.
Korean Standards Association. 2021. KS F 2081 Cross laminated timber. The Ministry of Knowledge Economy, Korean Agency for Technology and Standards, Seoul, Korea.
Kim, H.J. 2003. Polyurethane adhesives. Rubber Technology 4(2): 77-103.
Knorz, M., Torno, S., Kuilen, J.W. 2017. Bonding quality of industrially produced cross-laminated timber (CLT) as determined in delamination tests. Construction and Building Materials 133: 219-225.
Kramer, A., Barbosa, A.R., Sinha, A. 2014. Viability of hybrid poplar in ANSI approved cross-laminated timber applications. Journal of Materials in Civil Engineering 26(7): 06014009.
Kunniger, T., Clerc, G., Josset, S., Niemz, P., Pichelin, F., Kuilen, J.W.G. 2019. Influence of humidity and frequency on the energy dissipation in wood adhesives. International Journal of Adhesion and Adhesives 92: 99-104.
Li, H., Wang, B.J., Wei, P., Wang, L. 2019. Cross-laminated timber (CLT) in China: A state-of-the-art. Journal of Bioresources and Bioproducts 4(1): 22-31.
Mohamadzadeh, M., Hindman, D. 2015. Mechanical Performance of Yellow-poplar Cross Laminated Timber. Virginia Polytechnic Institute and State University, Blacksburg, VA, USA.
Na, J., Fan, Y., Tan, W., Guo, S., Mu, W. 2017. Mechanical behavior of polyurethane adhesive bonded joints as a function of temperature and humidity. Journal of Adhesion Science and Technology 32(5): 457-472.
Sterley, M., Trey, S., Lundevall, A., Olsson, S. 2012. Influence of cure conditions on the properties of a one-component moisture-cured polyurethane adhesive in the context of green gluing of wood. Journal of Applied Polymer Science 126(S1): E297-E304.
Tankut, N., Bardak, T., Sozen, E., Tankut, A.N. 2016. The effect of different nanoparticles and open time on bonding strength of poly (vinyl acetate) adhesive. Measurement 81: 80-84.
Yusof, N.M., Tahir, P.M., Lee, S.H., Khan, M.A., James, R.M.S. 2019. Mechanical and physical properties of cross-laminated timber made from Acacia mangiumwood as function of adhesive types. Journal of Wood Science 65(1): 20.
*원문 PDF 파일 및 링크정보가 존재하지 않을 경우 KISTI DDS 시스템에서 제공하는 원문복사서비스를 사용할 수 있습니다.
오픈액세스 학술지에 출판된 논문
※ AI-Helper는 부적절한 답변을 할 수 있습니다.