NTIS 바로가기Rare metal materials and engineering, v.42 no.6, 2013년, pp.1118 - 1122
Nannan, C. , Yi, F. , Jie, C. , Bin, L. , Fanyan, C. , Jingsong, Z.
Butt joints of aluminum foam were made by three different brazing processes including brazing with multilayer filler metal in high vacuum of 10-3 (Pa) degree, brazing with multilayer filler metal in low vacuum of 1 (Pa) degree and brazing with monolayer filler metal in high vacuum of 10-3 (Pa) degre...
Composite Structures[J] Hasan 83 180 2008 10.1016/j.compstruct.2007.04.016
Trans Nonferrous Met Soc China[J] Yu 17 93 2007 10.1016/S1003-6326(07)60054-5
Sci China[J] Ashby 46 6 521 2003 10.1360/02yb0203
Ashby 3 2000 Metals Foams A Design Guide[M]
Haferkamp 479 2001 Cellular Metals and Metal Foaming Technology[M]
Welt Int[J] Pogibenko 80 312 2001
Matthes 501 2001 Cellular Metals and Metal Foaming Technology[M]
Transactions of the China Welding Institution[J] Wang 29 10 1 2008
Adv Eng Mater[J] Born 5 11 121 2003
Mater Sci Eng A[J] Kizazono A327 128 2002 10.1016/S0921-5093(01)01766-X
Light Metals[J] Zhang 2 48 2006
Zhou 385 2006 Welding of Aluminum and Aluminum Alloy[M]
J Vac Sci Technol[J] Yu 29 68 2009
Acta Metallurgica Sinica[J] Wang 45 6 723 2009
Trans Nonferrous Met Soc China[J] Yu 16 1335 2006 10.1016/S1003-6326(07)60016-8