NTIS 바로가기Fatigue & fracture of engineering materials & structures, v.13 no.3, 1990년, pp.213 - 227
Couper, M. J. (Department of Materials Engineering, Monash University, Clayton, Victoria 3168, Australia) , Neeson, A. E. (Department of Materials Engineering, Monash University, Clayton, Victoria 3168, Australia) , Griffiths, J. R. (Department of Materials Engineering, Monash University, Clayton, Victoria 3168, Australia)
Abstract— The fatigue properties of un‐notched polished specimens of an aluminium casting alloy have been measured for various heat‐treatment conditions and at various mean stresses. The relation between fatigue life and alternating stress is insensitive to heat‐treatment and...
1 D. C. Jenkinson and L. M. Hogan ( 1975 ) The modification of aluminium‐silicon alloys with strontium . J. Cryst. Growth 28 , 171 – 187 .
2 D. S. Saunders , J. R. Griffiths and B. A. Parker ( 1975 ) The fracture toughness of an aluminium casting alloy . J. Aust. Inst. Metals 20 , 33 – 38 .
3 R. W. Coade ( 1980 ) The effect of second phase particles on the ductile failure of an Al‐Mg‐Si casting alloy . Ph.D. thesis , Monash University , Clayton , Australia .
4 M. J. Couper ( 1982 ) Fatigue of an Al‐Mg‐Si casting alloy . Ph.D. thesis , Monash University , Clayton , Australia .
5 L. P. Pook , A. G. Greenan , M. S. Found and W. J. Jackson ( 1980 ) Tests to determine the fatigue strength of steel castings containing shrinkage . J. Res. Steel Castings Res. Trade Assoc. 49 , 28 – 35 .
6 B. Östensso ( 1973 ) Influence of microshrinkage cavities on the endurance limit of nodular cast iron . J. Iron Steel Inst. 211 , 628 – 631 .
7 M. S. Starkey and P. E. Irving ( 1982 ) A comparison of the fatigue strength of machined and as‐cast surfaces of SG iron . Int. J. Fatigue 4 , 129 – 136 .
8 B. A. Parker , D. S. Saunders and J. R. Griffiths ( 1982 ) A quantitative evaluation of microstructure of a strontium‐modified Al‐Si‐Mg alloy following prolonged solution treatment . Metals Forum 5 , 48 – 53 .
9 P. R. Austen and H. M. Williamson ( 1975 ) The effects of non‐standard ageing treatments on the fracture properties of Al‐Mg‐7wt%Si alloys . J. Aust. Inst. Metals 20 , 39 – 43 .
10 R. B. Heyward ( 1962 ) Designing Against Fatigue . Chapman & Hall , London .
11 D. M. Smith and J. A. Eady ( 1981 ) Properties of CP601—a widely used aluminium foundry alloy . Proc. 34th Conf., Australian Inst. Metals, Brisbane (available from Comalco Research Centre , Thomastown , Australia ).
12 M. Katcher and M. Kaplan ( 1974 ) Effects of R‐factor and crack‐closure on fatigue crack growth for aluminium and titanium alloys . ASTM STP 559 , pp. 264 – 282 .
13 W. Elber ( 1970 ) Fatigue crack closure under cyclic tension . Engng Fract. Mech. 2 , 37 – 45 .
14 A. J. McEvily ( 1977 ) Current aspects of fatigue . Metal Set. J. 11 , 274 – 284 .
15 H. U. Staal and J. D. Elen ( 1979 ) Crack closure and influence of cycle ratio R on fatigue crack growth in type 304 stainless steel at room temperature . Engng Fract. Mech. 11 , 275 – 283 .
16 V. Bachman and D. Munz ( 1979 ) Fatigue crack closure evaluation with the potential method . Engng Fract. Mech. 11 , 61 – 71 .
17 N. E. Dowling ( 1977 ) Crack growth during low‐cycle fatigue of smooth axial specimens . ASTM STP 637 , pp. 97 – 121 .
18 D. Wilhem , J. FitzGerald , J. Carter and D. Dittmer ( 1981 ) An empirical approach to determining K for surface cracks . Proc. 5th. Int. Conf. on Fracture , Cannes , Vol. 1 , pp. 11 – 21 .
19 C. C. Wigant and R. I. Stephens ( 1987 ) Fatigue crack growth behaviour of A356‐T6 cast aluminium alloy . Fatigue 87 1 , 165 – 173 .
20 R. W. Landgraf , J. D. Morrow and T. Endo ( 1969 ) Determination of the cyclic stress‐strain curve . J. Mater. 4 , 176 – 188 .
21 S. Suresh and R. O. Ritchie ( 1984 ) Propagation of short fatigue cracks . Int. Metals Rev. 29 , 445 – 476 .
22 A. Fathulla , B. Weiss and R. Stickler ( 1984 ) Int. Spring Meeting on Crack Initiation Under Complex Loading , Paris , p. 182 , organized by the French Commission of Metal Fatigue.
*원문 PDF 파일 및 링크정보가 존재하지 않을 경우 KISTI DDS 시스템에서 제공하는 원문복사서비스를 사용할 수 있습니다.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.