In this study, we used a inductively coupled plasma (ICP) source for etching $Al_2O_3$ thin films because of its high plasma density, low process pressure and easy control bias power. $Al_2O_3$ thin films were etched using $Cl_2/BCl_3$, $N_2/Cl_2/BCl_3$, a...
In this study, we used a inductively coupled plasma (ICP) source for etching $Al_2O_3$ thin films because of its high plasma density, low process pressure and easy control bias power. $Al_2O_3$ thin films were etched using $Cl_2/BCl_3$, $N_2/Cl_2/BCl_3$, and Ar/$Cl_2/BCl_3$ plasma. The experiments were carried out measuring the etch rates and the selectivities of $Al_2O_3$ to $SiO_2$ as a function of gas mixing ratio, rf power, and chamber pressure. When $Cl_2$ 50% was added to $Cl_2/BCl_3$ plasma, the etch rate of the $Al_2O_3$ films was 118 nm/min. We also investigated the effect of gas addition. In case of $N_2$ addition, the etch rate of the $Al_2O_3$ films decreased while $N_2$ was added into $Cl_2/BCl_3$ plasma. However, the etch rate increased slightly as Ar added into $Cl_2/BCl_3$ plasma, and then further increase of Ar decreased the etch rate. The maximum etch rate was 130 nm/min at Ar 20% in $Cl_2/BCl_3$ plasma, and the highest etch selectivity was 0.81 in $N_2$ 20% in $Cl_2/BCl_3$ plasma. And, we obtained the results that the etch rate increases as rf power increases and chamber pressure decreases. The characteristics of the plasmas were estimated using optical emission spectroscopy (OES).
In this study, we used a inductively coupled plasma (ICP) source for etching $Al_2O_3$ thin films because of its high plasma density, low process pressure and easy control bias power. $Al_2O_3$ thin films were etched using $Cl_2/BCl_3$, $N_2/Cl_2/BCl_3$, and Ar/$Cl_2/BCl_3$ plasma. The experiments were carried out measuring the etch rates and the selectivities of $Al_2O_3$ to $SiO_2$ as a function of gas mixing ratio, rf power, and chamber pressure. When $Cl_2$ 50% was added to $Cl_2/BCl_3$ plasma, the etch rate of the $Al_2O_3$ films was 118 nm/min. We also investigated the effect of gas addition. In case of $N_2$ addition, the etch rate of the $Al_2O_3$ films decreased while $N_2$ was added into $Cl_2/BCl_3$ plasma. However, the etch rate increased slightly as Ar added into $Cl_2/BCl_3$ plasma, and then further increase of Ar decreased the etch rate. The maximum etch rate was 130 nm/min at Ar 20% in $Cl_2/BCl_3$ plasma, and the highest etch selectivity was 0.81 in $N_2$ 20% in $Cl_2/BCl_3$ plasma. And, we obtained the results that the etch rate increases as rf power increases and chamber pressure decreases. The characteristics of the plasmas were estimated using optical emission spectroscopy (OES).
* AI 자동 식별 결과로 적합하지 않은 문장이 있을 수 있으니, 이용에 유의하시기 바랍니다.
제안 방법
In this article, AI2O3 films were etched with CI2/BCI3 gas mixtures in an ICP, and the effect of N2 and Ar addition into CI2/BCI3 plasma was investigated. We measured the etch rate of AI2O3 films as a function of several etching parameters such as gas mixing ratio, rf power, chamber pressure.
To understand the etching mechanism, optical emission spectroscopy (OES) analysis was used for plasma diagnostic. OES was performed to analyze the behavior of active species as a function of gas mixing ratio, rf power, and chamber pressure.
The etch rate was estimated measuring the etched thickness with a surface profiler (KLA Tencor, a-step 500). The emission intensity of Cl atoms was investigated using an optical emission spectroscope (Nanotek NTS-U101) with the wavelength range of 300-800nm in order to understand the effects of the gas chemistry on the etch rate of AI2O3.
성능/효과
As results show in Fig. 2(a)t the etch rate of the AbCefilms decreased while N2 was added into CI2/BCI3 plasma, however, the etch selectivities reached the highest value (about 0.81) at N2 20% and then decreased. When Ar 20% added into CI2/BCI3 plasma, the etch rate increased slightly, and then further increase of Ar decreased the etch rate.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.