[특허]Chemically strengthened opal glass

Chemically strengthened opal glass 원문보기

IPC분류정보
국가/구분	United States(US) Patent 등록
국제특허분류(IPC7판)	B32B-017/00 C03C-021/00
출원번호	US-0706661 (1976-07-19)
발명자 / 주소	Rinehart Dale W. (Natrona Heights PA)
출원인 / 주소	PPG Industries, Inc. (Pittsburgh PA 02)
인용정보	피인용 횟수 : 27 인용 특허 : 0

초록 ▼

Opal glasses capable of being chemically strengthened by ion exchange with potassium are comprised of (by weight on the oxide basis): ________________________________ - Composition Percent by Weight ________________________________ SiO2 34 -60 Na2O 6 -23 K2O 0 -15 (Na2O +K2O) 18 -26 Al2O3 0 -18 ZrO2

대표청구항 ▼

A spontaneously opalized glass capable of being strengthened by ion-exchange with potassium ions, comprising by weight on the oxide basis: 34 to 60 percent SiO2 6 to 23 percent Na2O 0 to 15 percent K2O 18 to 26 percent (Na2O +K2O) 0 to 18 percent Al2O3 0 to 20 percent ZrO2 4 to 21 percent (Al2O3+ZrO2) 7 to 20 percent P2O5 0 to 9 percent CaO 0 to 9 percent SrO 2 to 9 percent (CaO +SrO) less than 0.1 percent Li2O said constituents comprising at least 90 percent by weight of the glass and proportioned relative to one another so as to provide the glass with a viscosity of 100 poises at a temperature less than 2800°F. (1538°C.). A chemically strengthened, spontaneously opalized glass article exhibiting a surface compressive stress after being subjected to surface abrasion composed of an interior portion which is in tension and surface compressive layer, said interior portion comprised of by weight on the oxide basis: 34 to 60 percent SiO2 6 to 23 percent Na2O 0 to 15 percent K2O 18 to 26 percent (Na2O +K2O) 0 to 18 percent Al2O3 0 to 20 percent ZrO2 4 to 21 percent (Al2O3 +ZrO3) 7 to 20 percent P2O5 0 to 9 percent CaO 0 to 9 percent SrO 2 to 9 percent (CaO +SrO) less tHan 0.1 percent Li2O said constituents comprising at least 90 percent by weight of said interior portion and proportioned relative to one another so as to provide the glass with a viscosity of 100 poises at a temperature less than 2800°F. (1538°C.), and said surface layer having a higher content of K2O and a lower content of Na2O than the interior portion. A method of strengthening an opal glass article comprising the steps of: a. contacting a source of potassium ions with the surface of a spontaneously opalized glass article comprising by weight on the oxide basis: 34 to 60 percent SiO2 6 to 23 percent Na2O 0 to 15 percent K2O 18 to 26 percent (Na2O +K2O) 0 to 18 percent Al2O3 0 to 20 percent ZrO2 4 to 21 percent (Al2O3 +ZrO2) 7 to 20 percent P2O5 0 to 9 percent CaO 0 to 9 percent SrO 2 to 9 percent (CaO +SrO) less than 0.1 percent Li2O said constituents comprising at least 90 percent by weight of the glass article and proportioned relative to one another so as to provide the glass with a viscosity of 100 poises at a temperature less than 2800°F. (1538°C.); b. heating said source of potassium ions while in contact with the glass to a temperature at which potassium ions from said source replace sodium ions in the glass, but essentially below the strain point of the glass, thereby creating a zone of compression at the surface of the glass which extends at least 5 microns into the glass; and c. removing the glass from contact with the potassium ion source.

이 특허를 인용한 특허 (27)

Charrue Herve,FRX ; Rifqi Francoise,FRX ; Crepet Renee,FRX ; Guillemet Claude,FRX, Chemically toughened pane.
상세보기
Weeks, Wendell P.; Schaut, Robert Anthony; DeMartino, Steven Edward; Peanasky, John Stephen, Delamination resistant pharmaceutical glass containers containing active pharmaceutical ingredients.
상세보기
Gross, Timothy Michael; Hu, Guangli; Roussev, Rostislav Vatchev; Smith, Charlene Marie; Tang, Zhongzhi; Tietje, Steven Alvin, Fusion formable glass-based articles including a metal oxide concentration gradient.
상세보기
DeMartino, Steven Edward; Fabian, Michelle Dawn; Kohli, Jeffrey Todd; Lyon, Jennifer Lynn; Smith, Charlene Marie; Tang, Zhongzhi, Glass articles exhibiting improved fracture performance.
상세보기
DeMartino, Steven Edward; Fabian, Michelle Dawn; Kohli, Jeffrey Todd; Lyon, Jennifer Lynn; Smith, Charlene Marie; Tang, Zhongzhi, Glass articles exhibiting improved fracture performance.
상세보기
Eliezer M. Rabinovich, Glass ferrule optical fiber connectors.
상세보기
Hayashi Ichiro,JPX ; Maeda Kei,JPX ; Mannami Kazuo,JPX, Glass substrate for magnetic disk.
상세보기
Dejneka, Matthew John; Gomez, Sinue; Hu, Guangli; Smith, Charlene Marie; Tang, Zhongzhi; Tietje, Steven Alvin, Glass-based articles including a metal oxide concentration gradient.
상세보기
Hu, Guangli; Smith, Charlene Marie; Tang, Zhongzhi; Tietje, Steven Alvin, Glasses and glass ceramics including a metal oxide concentration gradient.
상세보기
Hu, Guangli; Smith, Charlene Marie; Tang, Zhongzhi; Tietje, Steven Alvin, Glasses and glass ceramics including a metal oxide concentration gradient.
상세보기
Bennett, Kevin Wallace; Bickham, Scott Robertson; Derick, James A; Watkins, Percil, High numerical aperture multimode optical fiber.
상세보기
Rinehart Dale W. (Natrona Heights PA), Ion exchange strengthening of soda-lime-silica glass.
상세보기
Boek, Heather Debra; Weller, Mark Owen; Youngman, Randall Eugene, Ion exchangeable alkali aluminosilicate glass articles.
상세보기
Gross, Timothy Michael, Ion exchangeable glass with high crack initiation threshold.
상세보기
Gross, Timothy Michael, Ion exchangeable glass with high crack initiation threshold.
상세보기
Gross, Timothy Michael, Ion exchangeable glass with high crack initiation threshold.
상세보기
Gross, Timothy Michael, Ion exchangeable glass with high crack initiation threshold.
상세보기
Chapman, Christy Lynn; Dejneka, Matthew John; Gomez, Sinue; Lamberson, Lisa Ann, Ion exchangeable glasses.
상세보기
Chapman, Christy Lynn; Dejneka, Matthew John; Gomez, Sinue; Lamberson, Lisa Ann, Ion exchangeable glasses.
상세보기
Hnat James G. ; Mathur Akshay ; Simpson James C., Manufacture of ceramic tiles from fly ash.
상세보기
Miyasaka, Junko; Ohara, Seiki; Sakagami, Takahiro, Manufacturing method for phase-separated glass, and phase-separated glass.
상세보기
Frank Robert G. (Sarver PA) Moyer Kathleen L. (Allison Park PA), Method of fabricating a curved glass panel having a removable section and glass panel with a removable section.
상세보기
Rabinovich Eliezer M., Methods of making glass ferrule optical fiber connectors.
상세보기
Miyasaka, Junko; Sakagami, Takahiro; Ohara, Seiki; Akatsuka, Kosho; Diaz, Manuel Reyes; Ono, Kazutaka; Hijiya, Hiroyuki, Process for producing chemically strengthened glass.
상세보기
Murata, Takashi, Tempered glass substrate and method of producing the same.
상세보기
Murata, Takashi, Tempered glass substrate and method of producing the same.
상세보기
Miyasaka, Junko; Ohara, Seiki, White glass.
상세보기

내보내기 메뉴

내보내기 구분

파일저장
인쇄
메일전송

구성항목

기본정보
상세정보

관리번호, 국가코드, 자료구분, 상태, 출원번호, 출원일자, 공개번호, 공개일자, 등록번호, 등록일자, 발명명칭(한글), 발명명칭(영문), 출원인(한글), 출원인(영문), 출원인코드, 대표IPC

저장형식

Text(ASCII format)
Excel format
PIAS분석(.xls)

메일정보

받는사람 (필수): @
보내는사람 (선택): @
제목
내용: KISTI 검색결과 이메일 서비스

안내

총 건의 자료가 검색되었습니다.

다운받으실 자료의 인덱스를 입력하세요. (1-10,000)

검색결과의 순서대로 최대 10,000건 까지 다운로드가 가능합니다.

데이타가 많을 경우 속도가 느려질 수 있습니다.(최대 2~3분 소요)

다운로드 파일은 UTF-8 형태로 저장됩니다.
파일의 내용이 제대로 보이지 않을실 때는 웹브라우저 상단의 보기 -> 인코딩 -> 자동선택 여부를 확인하십시오.

Text(ASCII format)
Excel format

AI-Helper ※ AI-Helper는 을 사용합니다.

AI-Helper

안녕하세요, AI-Helper입니다. 좌측 "선택된 텍스트"에서 텍스트를 선택하여 요약, 번역, 용어설명을 실행하세요.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.

IPC	Description
A	생활필수품
A62	인명구조; 소방(사다리 E06C)
A62B	인명구조용의 기구, 장치 또는 방법(특히 의료용에 사용되는 밸브 A61M 39/00; 특히 물에서 쓰이는 인명구조 장치 또는 방법 B63C 9/00; 잠수장비 B63C 11/00; 특히 항공기에 쓰는 것, 예. 낙하산, 투출좌석 B64D; 특히 광산에서 쓰이는 구조장치 E21F 11/00)
A62B-1/08	.. 윈치 또는 풀리에 제동기구가 있는 것

연합인증

Chemically strengthened opal glass 원문보기

초록 ▼

대표청구항 ▼

연구과제 타임라인

이 특허를 인용한 특허 (27)

관련 콘텐츠

특허 원문 보기

IPC 상위 출원인

AI-Helper ※ AI-Helper는 오픈소스 모델을 사용합니다.

선택된 텍스트

내보내기 구분	파일저장 인쇄 메일전송
구성항목	기본정보 상세정보 관리번호, 국가코드, 자료구분, 상태, 출원번호, 출원일자, 공개번호, 공개일자, 등록번호, 등록일자, 발명명칭(한글), 발명명칭(영문), 출원인(한글), 출원인(영문), 출원인코드, 대표IPC 관리번호, 국가코드, 자료구분, 상태, 출원번호, 출원일자, 공개번호, 공개일자, 공고번호, 공고일자, 등록번호, 등록일자, 발명명칭(한글), 발명명칭(영문), 출원인(한글), 출원인(영문), 출원인코드, 대표출원인, 출원인국적, 출원인주소, 발명자, 발명자E, 발명자코드, 발명자주소, 발명자 우편번호, 발명자국적, 대표IPC, IPC코드, 요약, 미국특허분류, 대리인주소, 대리인코드, 대리인(한글), 대리인(영문), 국제공개일자, 국제공개번호, 국제출원일자, 국제출원번호, 우선권, 우선권주장일, 우선권국가, 우선권출원번호, 원출원일자, 원출원번호, 지정국, Citing Patents, Cited Patents
저장형식	Text(ASCII format) Excel format PIAS분석(.xls)
메일정보	받는사람 (필수) @ 보내는사람 (선택) @ 제목 내용 KISTI 검색결과 이메일 서비스
안내	총 건의 자료가 검색되었습니다. 다운받으실 자료의 인덱스를 입력하세요. (1-10,000) 검색결과의 순서대로 최대 10,000건 까지 다운로드가 가능합니다. 데이타가 많을 경우 속도가 느려질 수 있습니다.(최대 2~3분 소요) 다운로드 파일은 UTF-8 형태로 저장됩니다. 파일의 내용이 제대로 보이지 않을실 때는 웹브라우저 상단의 보기 -> 인코딩 -> 자동선택 여부를 확인하십시오. ~ Text(ASCII format) Excel format

연합인증

Chemically strengthened opal glass 원문보기

초록 ▼

대표청구항 ▼

연구과제 타임라인

전체(0) 논문(0) 특허(0) 보고서(0)

전체(0) 논문(0) 특허(0) 보고서(0)

이 특허를 인용한 특허 (27)

관련 콘텐츠

특허 원문 보기

IPC 상위 출원인

AI-Helper ※ AI-Helper는 오픈소스 모델을 사용합니다.

선택된 텍스트