초록 ▼

A sealing glass composition comprises a PbO-containing glass frit, two particulate refractory fillers having controlled particle size distributions, and optionally at least one additive to prevent the chemical reduction of the PbO when the frit is fired in the presence of reducing conditions. The se

A sealing glass composition comprises a PbO-containing glass frit, two particulate refractory fillers having controlled particle size distributions, and optionally at least one additive to prevent the chemical reduction of the PbO when the frit is fired in the presence of reducing conditions. The sealing glass composition is useful as a package sealant. It is especially useful as a solder glass for sealing a face plate portion to a funnel portion of a color television picture tube at temperatures of about 400°C. A particulate glass composition for use in preparing the sealing glass composition, a sealing glass paste and methods of using the sealing glass and paste are provided.

대표청구항 ▼

The method of sealing a faceplate to a funnel portion of a color television picture tube with a PbO-containing sealing glass in the presence of organic vapors capable of reducing the PbO in said sealing glass, comprising the steps of: a. applying between the mating sealing edges of said faceplate po

The method of sealing a faceplate to a funnel portion of a color television picture tube with a PbO-containing sealing glass in the presence of organic vapors capable of reducing the PbO in said sealing glass, comprising the steps of: a. applying between the mating sealing edges of said faceplate portion having phosphors and organic compounds which give off organic vapors when heated associated with said phosphors applied on an inner surface thereof and said funnel portion a sealing amount of a sealing glass composition comprising, i. at least about 70 weight percent of a PbO containing glass frit component having a sealing temperature of about 350°C. to about 415°C., ii. at least about 10-25 weight percent of at least one coarse particulate refractory filler component having a coefficient of thermal expansion of less than about 65 ×10-7 in./in./°C. (0°-300°C.) and a particle size distribution of about: ________________________________ -% of Particles Microns ________________________________ 90 40-60 75 30-45 50 15-35 25 7-20 10 2-10 5 0.5-3 ________________________________ iii. at least one additive in an amount sufficient to prevent the PbO in said glass frit from being chemically reduced upon exposure of said glass frit to reducing conditions at the sealing temperature thereof, said additive being selected from a group consisting of: 1. a hydroxide or a higher oxide of a cation, wherein the hydroxide and oxide are thermally stable at the sealing temperature of the frits, and further wherein the hydroxide and the oxide are capable of being chemically reduced when exposed to the reducing conditions; 2. an inorganic nitrate having a thermal deComposition temperature of about 30°-600°C., a melting point temperature of about 36°-264°C. and containing water of hydration; 3. an inorganic nitrate having a melting point temperature lower than the firing temperature of the PbO-containing glass frit and a thermal decomposition temperature higher than the firing temperature of the PbO-containing glass frit; 4. an inorganic nitrate having a melting point of about 414°-592°C.; 5. an inorganic nitrate which is thermally decomposable between about 150°C. and the fiber softening point temperature of the glass frit to yield HNO3; 6. an inorganic carbonate which is thermally decomposable to yield carbon dioxide above the firing temperature of the glass frit; 7. an inorganic, oxygen-containing chlorine compound having a thermal decomposition temperature above the firing temperature of the glass frit; and 8. an inorganic dichromate having a decomposition temperature of not more than about 100°C. below to not more than about 100°C. above the firing temperature of the glass frit; and iv. at least about 0.25-10 weight percent of at least one fine particulate refractory filler component having a coefficient of thermal expansion of less than about 65 ×10-7 in./in./°C. (0°-300°C.) and a particle size distribution of about: ________________________________ -% of Particles Microns ________________________________ 90 5-10 75 3-8 50 2-4 25 0.8-2.5 10 0.5-2.0 5 0.2-1.5 ________________________________ b. subjecting the faceplate portion and funnel portion and sealing glass composition to a temperature sufficient to fuse the sealing glass composition onto the faceplate portion and funnel portion, while simultaneously baking the faceplate and funnel, including the phosphors and organic compounds thereby resulting in the liberation of said organic vapors, and c. cooling the resulting assembly comprising the faceplate, funnel and sealing glass.