초록 ▼

A thin, laminar carbon member made of carbon or graphite felt impregnated with a carbonaceous, hardenable, cokable binder is hardened under the action of pressure and temperature and subsequently coked or graphitized in such a way that the carbon or graphite felt is only partially impregnated with t

A thin, laminar carbon member made of carbon or graphite felt impregnated with a carbonaceous, hardenable, cokable binder is hardened under the action of pressure and temperature and subsequently coked or graphitized in such a way that the carbon or graphite felt is only partially impregnated with the binder, i.e. with a solution of impregnating agent which is at least partially driven out of the cavities in the felt, but so that a thin coating of impregnating agent remains on the felt fibres, whereafter the felt returns to its original shape, is dried and then compressed to the desired thickness, during which the impregnating agent simultaneously condenses, whereafter the carbon member is calcined and graphitized. The such manufactured partially impregnated carbon member has a gross density of 0.1 to 0.8 g/cm3 and a thickness of 0.1 to 5 mm, the ratio of the area to the thickness of the plate being at least 105.

대표청구항 ▼

A thin laminar porous carbon member having a gross density of 0.1 to 0.8 gm/cm, a thickness of 0.1 to 5 mm and a ratio of surface area to thickness of at least 105 produced by carbonizing a carbon fiber felt impregnated with a heat and pressure hardened carbonaceous binder coating substantially all

A thin laminar porous carbon member having a gross density of 0.1 to 0.8 gm/cm, a thickness of 0.1 to 5 mm and a ratio of surface area to thickness of at least 105 produced by carbonizing a carbon fiber felt impregnated with a heat and pressure hardened carbonaceous binder coating substantially all the carbon fibers of the felt in such a manner that the porosity of the felt is retained. A method of forming a thin carbon member from a hardenable binder and porous carbon felt, said carbon felt being formed of carbon fibers, said method comprising the steps of; (a) impregnating said porous felt with a carbonaceous, hardenable and cokable binder such that substantially all of said fibers are coated with said binder; (b) eliminating some of said binder from said porous felt to the extent that said impregnated felt is porous; and (c) hardening said binder with heat and pressure to produce a rigid, partially impregnated, porous carbon member (d) carbonizing said member by heating to produce a rigid, high strength, dimensionally stable and porous carbon member having a gross density of 0.1 to 0.8 g/cm, a thickness of 0.1 to 5 mm, and a surface area to thickness ratio of at least 105. A method comprising the step of binding a plurality of thin laminar carbon members produced by the method of claim 7.