초록 ▼

The multi-layer polyester/polyolefin shrink film of this invention provides a combination of shrink tension, hot seal strength, sealability, and shrink temperature range heretofore unobtainable in an oriented, monolayer polyolefin material. The preferred film has five layers in which the middle laye

The multi-layer polyester/polyolefin shrink film of this invention provides a combination of shrink tension, hot seal strength, sealability, and shrink temperature range heretofore unobtainable in an oriented, monolayer polyolefin material. The preferred film has five layers in which the middle layer comprises a polyester or copolyester, two inner layers adjacent the middle layer comprise ethylene-vinyl actate copolymer, and the skin or outer layers comprise an ethylene-propylene copolymer.

대표청구항 ▼

A process for producing a heat shrinkable polyolefin packaging film having moderate shrink tension comprising the steps of: (A) coextruding at least three layers of polymeric material concentrically to form a multi-wall tube: (1) at least one of said layers being an inner layer and comprising a poly

A process for producing a heat shrinkable polyolefin packaging film having moderate shrink tension comprising the steps of: (A) coextruding at least three layers of polymeric material concentrically to form a multi-wall tube: (1) at least one of said layers being an inner layer and comprising a polymer selected from the group consisting of: (a) homopolymers, copolymers, and terpolymers of ethylene and (b) blends of ethylene homopolymers or copolymers with butylene homopolymers or copolymers, said inner layer comprising 47% to 90% of the total thickness of said laminate; (2) Another of said layers comprising a polymer selected from the group consisting of polyesters and copolyesters; (B) rapidly cooling said extruded tube; (C) heating said extrudate to a temperature in the range of 80°C. to 200°C.; (D) biaxially stretching said heated tube until it has a total wall thickness in the range of 0.1 mil to 2.0 mil; and, (E) rapidly cooling said tube while so stretched whereby the resulting shrink tension in the multi-layer film prepared by slitting said tube is in the range from about 100 p.s.i. to about 400 p.s.i.