초록 ▼

An absorbent resin composition obtained by copolymerizing in an aqueous solution a mixture of 100 parts by weight of an acrylate salt monomer (B) composed of 0 to 50 mol % of acrylic acid and 50 to 100 mol % of an alkali metal acrylate and 0.001 to 5 part by weight of a crosslinkable monomer (C) hav

An absorbent resin composition obtained by copolymerizing in an aqueous solution a mixture of 100 parts by weight of an acrylate salt monomer (B) composed of 0 to 50 mol % of acrylic acid and 50 to 100 mol % of an alkali metal acrylate and 0.001 to 5 part by weight of a crosslinkable monomer (C) having 2 to 4 groups selected from the group consisting of CH2〓CHCO－, CH2〓C(CH3)C0－and CH2〓CH-CH2－in the molecule in the presence of at least one surface-active agent (A) selected from the group consisting of water-soluble surface-active agents and water-dispersible surface-active agents in the presence of a water-soluble radical polymerization initiator while maintaining the initial concentration of said mixture in the range of from 25% by weight to saturation, and then drying the resulting gel-like hydrous polymer under heat; and an absorbent resin composition obtained by pulverizing said absorbent resin composition to form a resin powder, and blending said resin powder with 0.01 to 10 parts by weight, per 100 parts by weight of said resin powder, of ultra-microscopic silica having a specific surface area, measured by the Brunauer-Emmett-Teller method, of at least 50 m2/g and a particle diameter of not more than about 0.05 micron: and a process for producing the same.

대표청구항 ▼

A process for producing an absorbent resin composition, which comprises copolymerizing in aqueous solution a mixture of 100 parts by weight of an acrylate salt monomer (B) composed of 0 to 50 mol% of acrylic acid and 50 to 100 mol% of an alkali metal acrylate and 0.001 to 5 part by weight of a cross

A process for producing an absorbent resin composition, which comprises copolymerizing in aqueous solution a mixture of 100 parts by weight of an acrylate salt monomer (B) composed of 0 to 50 mol% of acrylic acid and 50 to 100 mol% of an alkali metal acrylate and 0.001 to 5 part by weight of a crosslinkable monomer (C) having 2 to 4 groups selected from CH2〓CHCO－, CH2〓C(CH3)CO－and CH2〓CH－CH2－in the molecule in the presence of at least one surface-active agent (A) selected from water-soluble surface-active agents and water-dispersible surface-active agents in the presence of a water-soluble radical polymerization initiator while maintaining the initial concentration of said mixture at 25% by weight to saturation; and drying the resulting gel-like hydrous polymer under heat. A process for producing an absorbent resin composition, which comprises copolymerizing in aqueous solution a mixture of 100 parts by weight of an acrylate salt monomer (B) composed of 0 to 50 mol% of acrylic acid and 50 to 100 mol% of an alkali metal acrylate and 0.001 to 5 part by weight of a crosslinkable monomer (C) having 2 to 4 groups selected from CH2〓CHCO－, CH2〓C(CH3)CO－and CH2〓CH－CH2－in the molecule in the presence of at least one surface-active agent (A) selected from water-soluble surface-active agents and water-dispersible surface-active agents in the presence of a water-soluble radical polymerization initiator while maintaining the initial concentration of said mixture at 25% by weight to saturation, drying the resulting gel-like hydrous polymer under heat, followed by pulverization, and then blending the resulting resin powder (D) with 0.01 to 10 parts by weight, per 100 parts by weight of the powder, of ultramicroscopic silica (E) having a specific surface area, measured by the Brunauer-Emmett-Teller method, of at least about 50 m2/g and a particle diameter of not more than about 0.05 micron.