초록 ▼

A laminated tubular structure is obtained by a process in which a fabric sleeve is applied about a tube of thermoplastic polymer, following which plugs are inserted into the opposing ends of the liner. A liquid, such as water, is then introduced to the liner, and the liner is rotated about a horizon

A laminated tubular structure is obtained by a process in which a fabric sleeve is applied about a tube of thermoplastic polymer, following which plugs are inserted into the opposing ends of the liner. A liquid, such as water, is then introduced to the liner, and the liner is rotated about a horizontal axis while heat is applied to the exterior surface of the liner, causing the surface to become molten. The heat also causes vaporization of some of the liquid in the liner and the resulting vapor pressure causes the molten surface of the liner to expand radially into the interstices of the fabric sleeve. The inner surface of the liner remains solid and form-maintaining by reason of the liquid within the liner and heat absorbed on vaporization of liquid. Upon cooling there is obtained a good mechanical bond between the liner and sleeve. The liner-sleeve composite can be further reinforced by a surrounding layer of a thermosetting resin containing reinforcing fibers, the resin layer being bonded to the composite by means of the sleeve.

대표청구항 ▼

A process for forming a laminated tubular structure which comprises: (a) applying a sleeve of a fabric about a tube of thermoplastic polymer, (b) inserting a plug into each end of said liner to seal the interior of said liner from the surrounding atmosphere, at least one of said plugs having pressur

A process for forming a laminated tubular structure which comprises: (a) applying a sleeve of a fabric about a tube of thermoplastic polymer, (b) inserting a plug into each end of said liner to seal the interior of said liner from the surrounding atmosphere, at least one of said plugs having pressure relief valve means to prevent the pressure of vaporized liquid within said liner from exceeding a given value upon heating said liner and sleeve to elevated temperatures, (c) introducing to said liner a liquid which is chemically inert with respect to said liner and has a boiling point substantially below the melting point of said thermoplastic polymer, (d) applying heat to an arcuate portion of the outer surface of said liner through said sleeve while rotating said liner and sleeve, the time of heating and the rates of application of heat and rotation of said liner and sleeve being such as to cause the exterior surface of said liner to melt and volatilization of a portion of said liquid to create a pressure within said liner which exceeds the pressure of the atmosphere external of said liner to cause said liner to expand radially whereby the molten exterior surface thereof enters into the interstices of said fabric, said liquid within said liner providing a temperature gradient across the wall of said liner whereby the inner surface thereof remains solid and self-supporting, and (e) cooling said liner to solidify the exterior surface thereof to produce a permanent mechanical bond between said sleeve and the outer surface of said liner. A process for forming a corrosion-resistant laminated tubular structure which comprises: (a) applying a sleeve of glass fabric about a seamless tube of thermoplastic fluorinated polymer, (b) inserting a plug into each end of said liner to seal the interior of said liner from the surrounding atmosphere, at least one of said plugs having pressure relief valve means to prevent the pressure of vaporized liquid within said liner from exceeding a predetermined value upon heating said liner and sleeve to elevated temperatures, (c) introducing water to said liner, (d) rotating said liner and sleeve about a substantially horizontal axis, and applying heat to an arcuate portion of the outer surface of said liner through said sleeve, the time of heating and the rates of application of heat and rotation of said liner and sleeve being such as to cause the exterior surface of said liner to melt the volatilization of a portion of said water to create a pressure of from about 0.1 to about 10 psig within said liner, to cause said liner to expand radially whereby the molten exterior surface thereof enters into the interstices of said fabric, said water within said liner providing a temperature gradient across the wall of said liner whereby the inner surface thereof remains solid and self-supporting, and (e) cooling said liner to solidify the exterior surface thereof to produce a permanent mechanical bond between said sleeve and the outer surface of said liner.