초록 ▼

Progressive burning propellant granules are prepared by a process in which the solvent-wet propellant granules are wetted with a mixture of burning rate deterrent and solvent. The burning rate deterrent penetrates the solvent-wet granules. After deterrent coating, the granules are dried to remove pr

Progressive burning propellant granules are prepared by a process in which the solvent-wet propellant granules are wetted with a mixture of burning rate deterrent and solvent. The burning rate deterrent penetrates the solvent-wet granules. After deterrent coating, the granules are dried to remove processing solvents initially present in the granules.

대표청구항 ▼

A process for preparation of progressive burning propellant granules of the single base, double base and triple base types from solvent-wet granules cut from propellant strands coming from the extrusion step in the propellant manufacturing process and prior to drying the solvent wet granules to remo

A process for preparation of progressive burning propellant granules of the single base, double base and triple base types from solvent-wet granules cut from propellant strands coming from the extrusion step in the propellant manufacturing process and prior to drying the solvent wet granules to remove processing solvents, said process comprising: (a) wetting all surfaces of the solvent-wet propellant granules with a mixture of burning rate deterrent and solvent, said burning rate deterrent being selected from dimethyl diphenyl urea, diethyl diphenyl urea, ethylene dimethacrylate, lead-2-ethyl hexoate and linear polyesters capable of diffusing into said propellant granule, said polyesters having a weight average molecular weight of from about 1,500 to about 30,000, melting point not exceeding 190°F. and being substantially nonmigrating within said propellant strand at temperatures below 150°F., and continuing wetting for a time sufficient to permit the burning rate deterrent to penetrate into the propellant granule, (b) promptly washing the resulting deterrent coated propellant granules with water to remove excess mixture of burning rate deterrent and solvent from the surfaces of said propellant granules, and (c) drying the resulting deterrent coated granules.