초록 ▼

A carbon fiber reinforced composite coil spring is provided which is made from a braid formed of carbon fibers oriented at a preferred angle to the braid axis of approximately plus or minus 45° and impregnated with a resin which serves as a substantially continuous matrix phase. Longitudinal reinfor

A carbon fiber reinforced composite coil spring is provided which is made from a braid formed of carbon fibers oriented at a preferred angle to the braid axis of approximately plus or minus 45° and impregnated with a resin which serves as a substantially continuous matrix phase. Longitudinal reinforcing fiber may be incorporated into the braid to prevent it from straightening under longitudinal tension. The carbon fiber reinforced composite coil spring is formed by wrapping the braid, impregnated with a non-solidified resin, within a groove which extends helically along the surface of a helical mandrel and solidifying the resinous matrix material, and then removing the solid composite coil spring from the helical mandrel.

대표청구항 ▼

1. A method for forming a carbon fiber reinforced composite coil spring comprising: (a) impregnating a carbon fiber braid wherein said carbon fibers are oriented at an angle in the range of approximately plus or minus 30° to plus or minus 60° to the braid axis and wherein there is incorporated in

1. A method for forming a carbon fiber reinforced composite coil spring comprising: (a) impregnating a carbon fiber braid wherein said carbon fibers are oriented at an angle in the range of approximately plus or minus 30° to plus or minus 60° to the braid axis and wherein there is incorporated into said braid a quantity of longitudinal reinforcing fibers which are oriented longitudinally to the braid axis so as to minimize change in said angle of said carbon fibers within said braid when placed under tension with a quantity of non-solidified resin to serve as a substantially continuous matrix material; (b) winding said impregnated braid in multiple layers while under longitudinal tension within a groove which extends helically along the surface of a cylindrical mandrel to provide the coil configuration of said carbon fiber reinforced composite coil spring; (c) solidifying the resinuous matrix material of the composite spring while maintaining said longitudinal tension; and (d) removing said solid spring from said mandrel. 2. The method of claim 1 wherein the angle of carbon fiber orientation is approximately plus or minus 45° to the braid axis. 3. The method of claim 1 wherein the longitudinal reinforcing fibers are selected from the group consisting of carbon fibers, glass fibers, aramid fibers, polyester fibers, natural fibers, and mixtures thereof. 4. The method of claim 1 wherein the quantity of longitudinal reinforcing fibers in said resulting carbon fiber reinforced composite coil spring is in the range of approximately 5 to 11 percent by volume. 5. The method of claim 1 wherein the resin is a thermosetting resin. 6. The method of claim 5 wherein the thermosetting resin is selected from the group consisting of polyester and epoxy resins. 7. The method of claim 5 wherein the quantity of thermosetting resin in said resulting carbon fiber reinforced composite coil spring is in the range of approximately 30 to 50 percent by weight. 8. The method of claim 1 wherein the shape of said groove is substantially rectangular. 9. The method of claim 1 wherein the sides of said groove are tapered to facilitate easy insertion and removal of said braid. 10. The method of claim 1 further including the step of treating the surface of said mandrel within said groove with a mold release material to facilitate the removal of the resulting carbon fiber reinforced composite coil spring from said groove after solidification. 11. The method of claim 1 wherein a collapsible mandrel is employed to facilitate the removal of said coil spring after solidification. 12. The method of claim 1 wherein said carbon fibers comprise graphitic carbon.