초록 ▼

A porous polyethylene film was obtained which is characterized in that micropores are contiguous with one another from one surface to the other surface of the film to constitute a laminar structure, and said micropores assume the form of strips being composed of microfibrils that are arrayed in a di

A porous polyethylene film was obtained which is characterized in that micropores are contiguous with one another from one surface to the other surface of the film to constitute a laminar structure, and said micropores assume the form of strips being composed of microfibrils that are arrayed in a direction in which the film is stretched and nodular portions that are coupled to said microfibrils nearly at right angles thereto, wherein the micropores have an average pore diameter over a range of 0.05 to 2 microns as measured using a mercury porosimeter, said film has a porosity over a range of 30 to 90%, and an elastic recovery factor from the 50% stretching ratio is less than 50%.

대표청구항 ▼

1. A porous polyethylene film comprising a series of microfibrils arrayed along the length of the film, a series of nodules disposed at substantially right angles to said microfibrils across the width of the film, said microfibrils and nodules defining micropores having an average pore diameter of 0

1. A porous polyethylene film comprising a series of microfibrils arrayed along the length of the film, a series of nodules disposed at substantially right angles to said microfibrils across the width of the film, said microfibrils and nodules defining micropores having an average pore diameter of 0.05 to 2 microns as measured by a mercury porosimeter, said microfibrils and nodules forming laminated strips wherein the micropores in said strips are contiguous with one another to provide pores extending from the surface of the film to the other, said film having a porosity of 30 to 90% and an elastic recovery factor from the 50% stretching ratio is less than 50%. 2. A porous polyethylene film according to claim 1, wherein the surface area is less than 30 m 2 /cm 3 . 3. A porous polyethylene film according to claim 1, wherein an average pore diameter of said micropores is greater than 0.5 micron. 4. A porous polyethylene film according to claim 1, wherein: (1) an average thickness (d M ) and an average length (l M ) of the microfibrils are given by: d M =0.01 to 0.5 micron l M =0.1 to 3.0 microns (2) an average length (l K ) of a modular portion comprising a group of micropores measured along the length of the film is given by l K =0.05 to 1.0 micron (3) an average width (d V ) and an average length (l V ) of the micropores are given by: ##EQU## 5. A process for the manufacture of a porous polyethylene film comprising molding a high-density polyethylene which has a melt index (MI value) of 0.1 to 5 and a density of greater than 0.955 g/cc 3 in a film extruder at a temperature which is higher by at least 20° C. than the melting point of the polymer but which does not exceed the melting point of the polymer by more than 80° C. and at a draft ratio of 10 to 5000 to prepare a film, annealing, as required, the thus obtained crystalline unstretched film at a temperature lower than the melting point of the polymer, cold-stretching the film by 5 to 100% through a stretching section maintained at a temperature lower than 40° C., hot-stretching the film through at least one stretching stage at a temperature range of 80° to 125° C., the total stretching in the cold-stretching and the hot-stretching stages being from 50 to 700%, and then, as required, thermally setting the film at a temperature of 100° to 125° C.