초록 ▼

A composite of diamond and cemented tungsten carbide is produced by placing pulverized diamond in adjacency with a tungsten carbide/cobalt composition. The two materials are separated by a metallic material positioned therebetween which material has a melting point, when so utilized, lower than the

A composite of diamond and cemented tungsten carbide is produced by placing pulverized diamond in adjacency with a tungsten carbide/cobalt composition. The two materials are separated by a metallic material positioned therebetween which material has a melting point, when so utilized, lower than the eutectic point of the tungsten carbide/cobalt composition. The assembly is heated at a temperature high enough to permit melting of the metallic material and in a pressure-temperature region of the carbon phase diagram where diamond is thermodynamically stable but which temperature is insufficient to cause substantial melting of the tungsten carbide/cobalt composition. In this way, a controlled amount of metal is introduced into the pulverized diamond to promote bonding thereof.

대표청구항 ▼

A method for producing a composite of diamond and cemented tungsten carbide, which method comprises: placing a layer consisting of pulverized diamond adjacent to a sintered tungsten carbide-cobalt support, said pulverized diamond and support being separated from each other by a second metallic mater

A method for producing a composite of diamond and cemented tungsten carbide, which method comprises: placing a layer consisting of pulverized diamond adjacent to a sintered tungsten carbide-cobalt support, said pulverized diamond and support being separated from each other by a second metallic material, said second metallic material having a melting point, when so utilized, below the eutectic point of said sintered tungsten carbide-cobalt support; heating said assembly to a temperature sufficiently high to cause the second metal to melt but not high enough to effect co-melting of the tungsten carbide and cobalt, said heating being effected in a pressure-temperature region of the carbon phase diagram where diamond is thermodynamically stable, and maintaining said temperature in said temperature-pressure region to join the diamond particles to each other and to join the diamond particles to said sintered tungsten carbide-cobalt support; and recovering a composite of diamond and cemented tungsten carbide.