초록 ▼

A method is described for producing articles having a metal core, an intermediate powder metallurgy layer, and an exterior wear- and chip-resistant layer on the portions thereof requiring the same, which comprises: applying to a bearing metal core, powdered steel alloy containing about 3.5% nickel b

A method is described for producing articles having a metal core, an intermediate powder metallurgy layer, and an exterior wear- and chip-resistant layer on the portions thereof requiring the same, which comprises: applying to a bearing metal core, powdered steel alloy containing about 3.5% nickel by weight by cold isostatic compaction in a compressible mold under a pressure of about 6000 atmospheres to provide an intermediate powder metallurgical layer having a density of about 90%; sintering said intermediate layer on said core in an atmosphere of hydrogen at about 1200°C. for about one hour; applying a wear- and chip-resistant layer to selected portions of said sintered intermediate powder metallurgical layer by plasma spraying; and hot isostatically compacting the sprayed article in a thin-walled deep-drawn vessel of low carbon steel having a wall thickness of about 0.5 mm in which the article to be compacted is surrounded by ceramic powder under a pressure of about 1600 atmospheres at a temperature of about 1100°C. for about two hours, to achieve a firm bond between said intermediate layer and said wear- and chip-resistant layer, and a composite density for said layers of about 99%.

대표청구항 ▼

In a method for producing articles having a metal core, an intermediate powder metallurgy layer, and an exterior wear- and chip-resistant layer on the portions thereof requiring the same, the improvement which comprises: applying to a bearing metal core, powdered steel alloy containing about 3.5% ni

In a method for producing articles having a metal core, an intermediate powder metallurgy layer, and an exterior wear- and chip-resistant layer on the portions thereof requiring the same, the improvement which comprises: applying to a bearing metal core, powdered steel alloy containing about 3.5% nickel by weight by cold isostatic compaction in a compressible mold under a pressure of about 6000 atmospheres to provide an intermediate powder metallurgical layer having a density of about 90%; sintering said intermediate layer on said core in an atmosphere of hydrogen at about 1200°C. for about one hour; applying a wear- and chip-resistant layer to selected portions of said sintered intermediate powder metallurgical layer by plasma spraying; and hot isostatically compacting the sprayed article in a thin-walled, deep-drawn vessel of low carbon steel having a wall thickness of about 0.5 mm in which the article to be compacted is surrounded by ceramic powder under a pressure of about 1600 atmospheres at a temperature of about 1100°C. for about two hours, to achieve a firm bond between said intermediate layer and said wear- and chip-resistant layer, and a composite density for said layers of about 99%.