초록 ▼

This invention relates to an improvement in filament winding large, hollow, tubular structures having significant axial reinforcement in their thick walls by means including (a) using a hollow, light weight mandrel adapted to expand radially at elevated temperatures and windings of alternate layers

This invention relates to an improvement in filament winding large, hollow, tubular structures having significant axial reinforcement in their thick walls by means including (a) using a hollow, light weight mandrel adapted to expand radially at elevated temperatures and windings of alternate layers of filamentary materials positioned substantially axially and substantially circumferentially relative to the longitudinal axis of the mandrel wherein the alternate layers are preferably in a certain thermosettable resin matrix and wound in certain fashion and (b) heating the filament wound mandrel to cure the thermosettable resin wherein heat from inside and out of the mandrel controls the cure and expansion during the heating step. The thick walls preferably incorporate graphite fibers for significant strength in the reinforcement provided by the filamentary materials.

대표청구항 ▼

A method of fabricating highly reinforced, hollow tubular structures with thick, dimensionally precise walls densely packed with filamentary materials in a substantially void free and uniformly dispersed thermoset resin, said tubular structures being of a size so large in length, diameter and wall t

A method of fabricating highly reinforced, hollow tubular structures with thick, dimensionally precise walls densely packed with filamentary materials in a substantially void free and uniformly dispersed thermoset resin, said tubular structures being of a size so large in length, diameter and wall thickness as to otherwise potentially subject them to distortions during filament winding and cure, said method comprising: (a) winding continuous filamentary materials about a hollow, thin walled, aluminum mandrel having a central longitudinal axis and ribs extending radially inward supported solely by the mandrel wall, said mandrel capable of radial expansion at elevated temperatures, said winding being performed so as to form a plurality of alternate layers comprising layers of windings which are substantially circumferential relative to said axis and layers of winding which are substantially axial windings of filamentary materials, said axial windings being at a small angle with respect to said axis and grouped in pairs of plies in which the first small angle of each of said plies in said pairs is the negative angle of the second small angle, each of said pairs being temporarily circumferentially bound by a wrap that is unwound during winding of the subsequent circumferentially winding of said substantially circumferentially wound layers while said pairs are additionally anchored at the ends of said mandrel, each of said alternate layers being in a matrix of thermosetting resin wherein an outer portion thereof radially away from said mandrel comprises an epoxy resin composition that gels below about 40°C. and an inner portion of said thermosetting resin between said mandrel and said outer portion comprises a non-gelling epoxy resin; (b) heating said filament wound mandrel to a temperature and for a time sufficient to cure the thermosettable resin, said heating being accomplished in an oven and in a manner such that the interior of said mandrel is raised through radiant heating thereat to a higher temperature than the temperature to which the exterior of the filament wound mandrel is exposed during said heating, said temperature difference being maintained during substantially the entire heating step said mandrel expanding during said heating; (c) cooling the resultant filament wound structure at a rate such that stresses in said structure resulting from contraction during cooling of said structure are minimized; (d) sliding said structure that has undergone said contraction off said mandrel.