초록 ▼

A method is provided for producing a catalytic structure in the form of sheet or honeycomb for the gas phase reduction of nitrogen oxides. The method comprises: beating an inorganic fiber in water to form a slurry; forming the slurry into a sheet by paper-making means and drying the sheet; impregnat

A method is provided for producing a catalytic structure in the form of sheet or honeycomb for the gas phase reduction of nitrogen oxides. The method comprises: beating an inorganic fiber in water to form a slurry; forming the slurry into a sheet by paper-making means and drying the sheet; impregnating the sheet or a honeycomb structure manufactured therefrom which has a porosity of 60-85% with an impregnating slurry which contains titanium dioxide or its precursor in a concentration at least of 100 g/l and has a viscosity of 5-250 cps. at normal temperatures, drying, and when necessary calcining the structure; and then immersing the structure in a solution containing a catalytically active agent or its precursor, drying and calcining the structure, thereby to provide a porous catalytic structure having titanium dioxide and the catalytically active agent substantially uniformly dispersed and supported therein.

대표청구항 ▼

A method for producing a catalyst structure in the form of porous sheet or honeycomb for the gas phase reduction of nitrogen oxides in the presence of ammonia, which comprises: (a) bearing at least one of inorganic fibers of about 1-20 mm in fiber length and of about 0.1-30 microns in average diamet

A method for producing a catalyst structure in the form of porous sheet or honeycomb for the gas phase reduction of nitrogen oxides in the presence of ammonia, which comprises: (a) bearing at least one of inorganic fibers of about 1-20 mm in fiber length and of about 0.1-30 microns in average diameter selected from the group consisting of ceramic fiber, silica fiber, silica-alumina fiber, chrysotile fiber, asbestos fiber, rock wool, glass fiber, anthophyllite fiber, potassium titanate fiber and carbon fiber, in water, to form a stock material containing the solid components in an amount of 1-10% by weight; (b) forming the stock material into a sheet by paper making means and drying to produce a sheet which has a void fraction of 65-80%; (c) impregnating the sheet or a honeycomb structure manufactured therefrom with an impregnating slurry containing titanium dioxide as a carrier material or its precursor which will be converted into titanium dioxide when calcined in a concentration at least of 100 g/l and having a viscosity of 5-250 cps. at normal temperature, drying, and when necessary calcining the structure; and (d) immersing the structure in a solution containing at least one catalytically active agent of an oxide selected from the group consisting of Cu, Fe, V, W and Mo or their precursors which will be converted into the oxides when calcined, drying and calcining the structure. The method as claimed in claim 1 wherein titanium dioxide or its precursor which will be converted into titanium dioxide when calcined is admixed with the stock material so that the stock material contains the solid components in an amount of about 1-10% by weight which consist of not more than about 40% by weight of titanium dioxide or its precursor and not less than about 60% by weight of the fiber. The method as claimed in claim 1 wherein the inorganic fiber is beaten together with a combustible organic fiber in amounts of about 1-30% by weight based on the inorganic fiber.