One step method of applying polysiloxane and PTFE coating composition
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
B05D-003/00
B05D-003/02
출원번호
US-0600993
(1984-04-16)
발명자
/ 주소
Kuziemka, Edmund J.
출원인 / 주소
Material Sciences Corporation
대리인 / 주소
Emrich & Dithmar
인용정보
피인용 횟수 :
7인용 특허 :
7
초록▼
Fast curing resin coating compositions for coating metal surfaces and a one-step method are described. The coatings comprise a high molecular weight epoxy resin, although a portion thereof may be low molecular weight, an effective amount of a cross-linking agent for the epoxy resin, a polysiloxane r
Fast curing resin coating compositions for coating metal surfaces and a one-step method are described. The coatings comprise a high molecular weight epoxy resin, although a portion thereof may be low molecular weight, an effective amount of a cross-linking agent for the epoxy resin, a polysiloxane resin system, an effective amount of a curing agent for the polysiloxane fluid system, a fluorocarbon polymer, and the balance being suitable solvents. The coatings are applied in one-step and dry in less than one minute and may be formed into various shapes and forms useful for stovetop cookware.
대표청구항▼
1. A one-step method of applying a fast curing resin coating composition to a metal substrate comprising: applying a thin film directly to said metal substrate, said thin film containing an epoxy resin having a molecular weight measured by gel permeation chromatography in the range of from about
1. A one-step method of applying a fast curing resin coating composition to a metal substrate comprising: applying a thin film directly to said metal substrate, said thin film containing an epoxy resin having a molecular weight measured by gel permeation chromatography in the range of from about 300 to about 200,000 present in the range of from about 10% by weight to about 20% by weight of said composition, not less than about 85% of the epoxy resin having a molecular weight in the range of from about 50,000 to about 200,000, an effective amount of a cross-linking agent for the epoxy resin, a polysiloxane resins system present in the range of from about 2% by weight to about 7% by weight of said composition, an effective amount of a curing agent for the polysiloxane resins system, polytetrafluoroethylene present in the range of from about 4% by weight to about 15% by weight of said composition, and the balance being suitable solvents, the film having a dry thickness in the range of from about 0.7 mils to about 1.2 mils, and curing the coating by heating the metal substrate to a temperature in the range of from about 450° F. to about 480° F. for a time of not greater than about one minute. 2. The method of claim 1, wherein the metal surface is pretreated with a degreasing agent. 3. The method of claim 1, wherein up to 15% by weight of the epoxy resin has a molecular weight measured by gel permeation chromatography in the range of from about 300 to about 500. 4. The method of claim 1, wherein the cross-linking agent is a melamine-formaldehyde resin or an etherified resol-type phenolic resin. 5. The method of claim 1 wherein the cross-linking agent is a urea formaldehyde. 6. The method of claim 1, wherein the cross-linking agent is present in the range of from about 10% to about 12% by weight of the solids content of the epoxy resin. 7. The method of claim 1, wherein the polysiloxane resin system includes a fluid mixture of methyphenylsiloxane, dimethysiloxane and diphenyldimethysiloxane. 8. The method of claim 1, wherein the polysiloxane resin system includes organopolysiloxanes or a precondensate which has one or more of the units ##STR## wherein X is a functional group which allows cross-linking at its site and a, b, c, d, e, are of a magnitude and proportions which provide the resin with a degree of substitution, measured as the ratio of phenyl plus methyl groups to silicon atoms, of at least about one and a ratio of phenyl groups to silicon atoms of at least about 0.3, and which has a silanol content above 4%, based on the weight of the precondensate. 9. The method of claim 8, wherein the curing agent for the polysiloxane resin system is a multi-functional amine catalyst or tin, zinc or iron salt of an organic acid. 10. The method of claim 9, wherein the salt of said organic acid is an octoate or a naphthenate. 11. The method of claim 9, wherein the curing agent for the polysiloxane resin system is dibutyltin dilaurate. 12. The method of claim 1, wherein essentially all of the epoxy resin has a molecular weight in the range of from about 50,000 to about 200,000. 13. The method of claim 1, wherein the epoxy resin is present in the range of from about 15% to about 20%. 14. The method of claim 1, wherein the suitable solvents include isophorone and butyl cellosolve. 15. The method of claim 1, and further including a surface tension modifier to control foaming and surface defects in the coating.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (7)
Kritzler Steven (Cronulla AUX), High fluorocarbon content coating composition, method of application, and coated article.
Wald David K. (Cherry Hill NJ), Process for applying coating composition comprising a polysiloxane resin-forming precondensate, an epoxy resin, a silico.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.