초록

Light-curable dentin and enamel adhesives comprising phosphorus-containing polymerizable monomer, sulfur compound having sulfur in the +2 or +4 oxidation state, selected photoinitiators, and an optional peroxide compound, as well as one-step and two-step curing methods.

대표청구항 ▼

1. A visible light cure dentin and enamel primer composition, comprising: (a) as a first component, phosphorous-containing free-radically polymerizable monomer suitable for use in the oral environment; (b) as a second component, sulfur compound having sulfur in the +2 or +4 oxidation state, sa

1. A visible light cure dentin and enamel primer composition, comprising: (a) as a first component, phosphorous-containing free-radically polymerizable monomer suitable for use in the oral environment; (b) as a second component, sulfur compound having sulfur in the +2 or +4 oxidation state, said second component acting as a polymerization activator for said first component and enhancing adhesion of said composition to dentin; and (c) as a third component, photoinitiator selected from substituted and unsubstituted alkylphenones, substituted and unsubstituted benzilidene acetophenones, and compounds of the formula: ##STR## wherein: X is nothing, a carbon-carbon bond, CR 2, C= 1, C=O, S, SO, SO 2, O, or NR where each R is independently H or a lower alkyl or substituted alkyl group and R 1 is a tetravalent unsaturated aliphatic radical doubly bonded to said C of C=R 1 and bonded to the 4 or 5 position of said Formula I to form a fused ring structure; Y and Z are independently lower alkyl, substituted alkyl, a divalent unsaturated radical bonded to adjacent positions of said Formula I to form a fused ring structure, alkoxy, halogen, or nitro; and m and n are independently zero to 4. 2. A composition according to claim 1, wherein said polymerizable monomer contains phosphorus atoms bonded to one or more olefinically unsaturated groups and bonded to one or more chlorine atoms, bromine atoms, active hydrogen atoms, or alkyl, substituted alkyl, allyl, or substituted allyl groups. 3. A composition according to claim 1, wherein said polymerizable monomer comprises an organic ester of one or more acids of phosphorus, the organic radical of said ester containing at least one free-radically polymerizable functional group, and wherein said ester has chlorine or bromine bonded directly to phosphorus. 4. A composition according to claim 1, wherein said polymerizable monomer is selected from (a) 2-methacryloxyethyl phenyl phosphate, and (b) halophosphorus ester wherein the organic radical of said ester is the residue remaining after removal of one or more hydroxyl hydrogen atoms from BIS-GMA, phosphorus is doubly bonded to an oxygen atom, is bonded to at least one chlorine atom, and the ratio of said phosphorus to said BIS-GMA is between about 0.015:1 and 1:1. 5. A composition according to claim 1, wherein said sulfur compound comprises an alkali metal salt or ammonium salt of a sulfinate, sulfite, sulfonate, bisulfite, metabisulfite, or hydrosulfite anion, or the free acid counterpart thereof. 6. A composition according to claim 1, wherein said sulfur compound comprises sodium benzene sulfinate or para-toluene sulfinate. 7. A composition according to claim 1, wherein said photoinitiator comprises an alkylphenone or a benzilidene acetophenone. 8. A composition according to claim 1, wherein said photoinitiator comprises a compound of said Formula I. 9. A composition according to claim 1, wherein said photoinitiator comprises a xanthone or thioxanthone. 10. A composition according to claim 1, wherein said photoinitiator comprises 2-chlorothioxanthone. 11. A composition according to claim 1, further comprising an acyl or alkyl peroxide or hydroperoxide, or a diacyl or dialkyl peroxide. 12. A composition according to claim 1, further comprising benzoyl peroxide. 13. A composition according to claim 11, wherein said composition is in two parts, the first of said two parts containing said polymerizable monomer and said peroxide or hydroperoxide, the second of said two parts containing said sulfur compound, and either or both of said two parts containing said photoinitiator, and wherein said polymerizable monomer is about 5 to 95 percent by weight of said composition after said two parts are mixed, said sulfur compound is about 0.5 to 10 percent by weight of said polymerizable monomer, and said photoinitiator and said peroxide or hydroperoxide are each independently about 0.05 to 10 percent by weight of said polymerizable monomer. 14. A two-part visible light cure dentin primer, one part of which comprises a peroxide compound and the reaction product of BIS-GMA in a diluent with about 0.25 to 10 percent by weight, based on the weight of said BIS-GMA, of phosphorus oxychloride, and the second part of which is a liquid solution comprising alkali benzene sulfinate and 2-chlorothioxanthone. 15. A two-part visible light cure cavity liner, crown preparation or adhesive, one part of which comprises radioopaque filler, a peroxide compound, and the reaction product of BIS-GMA in a diluent with about 0.25 to 10 percent by weight, based on the weight of said BIS-GMA, of phosphorus oxychloride, and the second part of which is a liquid solution comprising alkali benzene sulfinate and 2-chlorothioxanthone.