초록 ▼

Methods and apparatus for vulcanizing rubber and like material (10). Ultrasonic energy at about 10 to 100 kilohertz is applied to the material (10) at an energy intensity sufficient to generate heat to a temperature in the range of about 200 to 300 degrees Fahrenheit, while a static pressure is appl

Methods and apparatus for vulcanizing rubber and like material (10). Ultrasonic energy at about 10 to 100 kilohertz is applied to the material (10) at an energy intensity sufficient to generate heat to a temperature in the range of about 200 to 300 degrees Fahrenheit, while a static pressure is applied on the material (10) sufficient to prevent substantial cavitation and material degradation. The application of the ultrasonic energy and the pressure is maintained for at least about 10 minutes for each 1/8 inch in thickness of the material (10).

대표청구항 ▼

1. A method of vulcanizing rubber and like material comprising applying ultrasonic energy to the material at an energy intensity sufficient to generate heat in the material to a temperature in the range of about 200 to 300 degrees Fahrenheit, applying a static pressure on the material sufficient

1. A method of vulcanizing rubber and like material comprising applying ultrasonic energy to the material at an energy intensity sufficient to generate heat in the material to a temperature in the range of about 200 to 300 degrees Fahrenheit, applying a static pressure on the material sufficient to prevent substantial cavitation and material degradation therein, and maintaining the application of the ultrasonic energy and the pressure for at least about 10 minutes for each 1/8 inch in thickness of the material. 2. A method as in claim 1, wherein the frequency of the ultrasonic energy is in the range of about 10 to 100 kilohertz. 3. A method as in claim 1, wherein the energy intensity is in the range of about 20 to 200 watts per square inch. 4. A method as in claim 1, wherein the energy is applied initially at a higher energy intensity and is decreased asymptotically to a lower energy intensity. 5. A method as in claim 4, wherein the higher energy intensity is about 100 to 200 watts per square inch and the lower energy intensity is about 20 to 80 watts per square inch. 6. A method as in claim 4, wherein the energy intensity is decreased to about 40 to 45 percent of its initial intensity in about 3 to 5 minutes. 7. A method as in claim 1, wherein the pressure is in the range of about 500 to 1000 pounds per square inch. 8. A method as in claim 1, wherein the time of maintaining the application of the energy and the pressure is about 10 to 60 minutes. 9. Apparatus for vulcanizing rubber and like material comprising means for applying and maintaining ultrasonic energy to the material at an energy intensity sufficient to generate heat in the material to a temperature in the range of about 200 to 300 degrees Fahrenheit, and means for applying and maintaining a static pressure on the material sufficient to prevent substantial cavitation and material degradation therein. 10. Apparatus as in claim 9, wherein the frequency of the ultrasonic energy is in the range of about 10 to 100 kilohertz. 11. Apparatus as in claim 9, wherein the energy intensity is in the range of about 20 to 200 watts per square inch. 12. Apparatus as in claim 9, wherein the energy applying and maintaining means comprises means for applying the ultrasonic energy initially at a higher energy intensity and means for decreasing it asymptotically to a lower energy intensity. 13. Apparatus as in claim 12, wherein the higher energy intensity is about 100 to 200 watts per square inch and the lower energy intensity is about 20 to 80 watts per square inch. 14. Apparatus as in claim 12, wherein the energy intensity decreasing means comprises means for decreasing the energy intensity to about 40 to 45 percent of its initial intensity in about 3 to 5 minutes. 15. Apparatus as in claim 9, wherein the pressure is in the range of about 500 to 1000 pounds per square inch. 16. Apparatus as in claim 9, wherein the time of maintaining the application of the energy and the pressure is about 10 to 60 minutes. 17. Apparatus as in claim 9, wherein the means for applying and maintaining the ultrasonic energy comprises an ultrasonic transducer, a booster horn energized by the transducer, and a coupling horn energized by the booster horn and contacting a surface of the material. 18. Apparatus as in claim 9, including a mold for holding the material. 19. Apparatus as in claim 18, wherein the means for applying and maintaining the static pressure comprises an adjustable spring or a hydraulic cylinder that presses against the mold. 20. Apparatus as in claim 18, wherein the mold comprises essentially a material that is mechanically strong, low in thermal conductivity, and low in absorptance of ultrasonic energy. 21. Apparatus as in claim 18, wherein the mold comprises essentially steel, titanium, or a ceramic.