초록 ▼

A composite dual wall cast urethane elastomer to metal thread protector that will be practical under normal as well as frigid temperature conditions of usage is formed by deep drawing a seamless metal shell wall, using a threaded die to define a mold cavity with the metal shell wall, forming and set

A composite dual wall cast urethane elastomer to metal thread protector that will be practical under normal as well as frigid temperature conditions of usage is formed by deep drawing a seamless metal shell wall, using a threaded die to define a mold cavity with the metal shell wall, forming and setting a synthetic elastomeric shell wall within the mold cavity in an adhering assembled relation with and along the metal shell wall with threading that is complementary with threading of the die, removing the assembly by unscrewing it with respect to the threaded die, and subjecting the assembly to heat treatment to cure the elastomeric shell wall and provide a composite protector having a cast urethane elastomer wall in a secure adhering encapsulating relation on the metal shell wall.

대표청구항 ▼

1. A method of making a composite elastomer to metal shell dual wall thread protector for a threaded end of a pipe member that is practical for use and reuse under elevated, normal and frigid temperature conditions which comprises, deepdraw forming a metal blank into an elongated cylindrical shell h

1. A method of making a composite elastomer to metal shell dual wall thread protector for a threaded end of a pipe member that is practical for use and reuse under elevated, normal and frigid temperature conditions which comprises, deepdraw forming a metal blank into an elongated cylindrical shell having a continuous substantially closed end wall and an opposite substantially open end wall, forming a casting assembly by placing the metal shell and its closed end wall in a cooperating mold cavity defining relation with respect to a hollow die having an opposed threaded side wall therealong, introducing a normally thermoplastic synthetic elastomer material in heat-liquidized form into and filling the mold cavity along the threaded wall of the die, solidifying by preliminarily heat-curing the elastomer material within the mold cavity as an adherent wall casting along the metal shell wall and forming a solidified elastomer to metal shell adherent dual wall assembly therewithin, then removing the hollow die by unscrewing the thus-formed elastomer to metal shell adherent dual wall assembly with respect to the die, thereafter subjecting the elastomer wall of the dual wall assembly to a final heat-curing treatment, and effecting the heat-curing in such a manner as to make the solidified elastomer wall fully thermosetting and to also improve its resistance to chemicals such as encountered in the oil fields. 2. A method as defined in claim 1 wherein, the elastomer material is heated to its liquidized form before it is introduced into the mold cavity, the elastomer material is solidified and preliminarily hardened within the mold cavity by applying heat to the casting assembly to form the adherent dual wall assembly with the metal shell before the hollow die is removed and the final curing treatment is thereafter effected by applying heat to the dual wall assembly. 3. A method as defined in claim 2 wherein the preliminary cure-hardening of the elastomer material within the mold cavity is effected by applying heat thereto at a temperature of about 200° F. for about fifteen minutes. 4. A method as defined in claim 3 wherein, after the hollow die has been removed with respect to the dual wall assembly, the elastomer wall casting of the dual wall assembly is subjected to a final curing treatment at about 200° F. for about sixteen hours. 5. A method as defined in claim 2 wherein, before the elastomer material is introduced into the mold cavity, an adhesive is applied to a side of the metal shell that defines the cooperating mold cavity with the hollow die, and the threaded wall of the die is provided with a mold release material applied thereto. 6. A method as defined in claim 1 wherein, the metal shell is deep-drawn to form a seamless metal cup, and a punch is applied to the closed end wall of the cup to form tool receiving apertures therein before the metal cup is placed within the hollow die. 7. A method as defined in claim 6 wherein the tool receiving apertures are employed in aligning and retaining the metal blank in a suitable mold cavity forming position within the hollow die. 8. A method as defined in claim 1 wherein, the mold cavity extends longitudinally along the opposed threaded side wall of the die and laterally inwardly with respect to the closed end wall of the metal shell for a distance corresponding to a desired overlapping end wall thickness of the dual wall assembly to thereby cast-form an end flange of the elastomer material with respect to the closed end wall of the metal shell. 9. A method as defined in claim 1 wherein, the hollow die is positioned in an inwardly spaced relation with respect to an inner side of the metal shell, and the threads are formed along an inner side wall of the elastomer material of the dual wall assembly by the die to provide a pin type of protector. 10. A method as defined in claim 1 wherein, the hollow die is positioned in an outwardly spaced relation with respect to an outer side of the metal shell, and the threads are formed along the outer side of the elastomer material of the dual wall assembly by the die to form a box type of protector.