초록 ▼

A method for producing the matrix for the embossing cylinder which has a uniform pattern design in the marginal areas adjoining the abutment where the ends of the blanket are joined to form the tube comprising (1) casting liquid silicone rubber on a sheet of leather having the desired grain and vulc

A method for producing the matrix for the embossing cylinder which has a uniform pattern design in the marginal areas adjoining the abutment where the ends of the blanket are joined to form the tube comprising (1) casting liquid silicone rubber on a sheet of leather having the desired grain and vulcanizing the silicone, (2) using the matrix thus formed to emboss, under heat and pressure in a press, a rectangular sheet of thermoplastic resin such as polyvinyl chloride film, (3) forming the embossed sheet into a tube, (4) placing the portion of the tube having abutting edges in a narrow platen press and reembossing the area surrounding the abutment with the silicone rubber matrix to mask the impression of the joint and provide a continuous uninterrupted pattern, and (5) using the positively-embossed thermoplastic sheet as a matrix for casting vulcanizable silicone rubber to form a negatively-embossed matrix for use as a blanket on an embossing roll. The embossing roll is used to produce continuous lengths of embossed thermoplastic film with a continuous, uninterrupted grain pattern.

대표청구항 ▼

1. A method for making an embossing cylinder having a silicone rubber surface with a negative impression of grain design which comprises (a) providing a sheet of natural leather having the desired grain design, (b) pouring liquid vulcanizable silicone rubber on to the grained surface to form a u

1. A method for making an embossing cylinder having a silicone rubber surface with a negative impression of grain design which comprises (a) providing a sheet of natural leather having the desired grain design, (b) pouring liquid vulcanizable silicone rubber on to the grained surface to form a uniformly thick coating, (c) vulcanizing the silicone rubber to provide an embossing matrix having an accurate negative impression of said grain design, (d) stripping said embossing matrix from said leather sheet, (e) laying a thermoplastic film, having opposed parallel edges, on the grained surface of said matrix and subjecting the film to heat and pressure to form a positive impression on the surface, (f) stripping the film from the matrix and forming it into a tube with the embossed surface on the outside and said parallel edges abutting, (g) placing said embossing matrix over said abutting edges and the marginal area on either side thereof, (h) subjecting the film beneath said matrix to heat and pressure to overemboss the previously embossed surface in said marginal areas, (i) pouring vulcanized silicone rubber on the embossed surface to form a uniformly thick blanket, (j) vulcanizing the silicone rubber blanket, (k) stripping the blanket from the embossed surface, and (l) adhering the blanket, embossed side out, to the surface of a cylinder. 2. The method of claim 1 in which said embossing of the thermoplastic film in steps (e) and (h) is effected in a press with flat platens. 3. The method of claim 1 in which said overembossing of the thermoplastic film in the marginal area is effected in a press with narrow, slightly-curved platens. 4. The method of claim 3 in which the embossing area of said pressing platens continuously increases in the circumferential direction of the tube toward the opposed edges of the pressing platens. 5. The method of claim 1 in which the tube of thermoplastic film, embossed side out, is connected to the outer surface of a cylinder, the cylinder continuously is rotated and the liquid vulcanizable silicone rubber is poured on the surface of the tube and then vulcanized. 6. The method of claim 1 in which the edges of said marginal area are curved, serpentine fashion. 7. The method of claim 1 which includes the step of laying a reinforcing fabric over said layer of silicone rubber before vulcanization. 8. The method of claim 1 in which the embossing is carried out at a temperature of at least 150° C., preferably between 180° C. and 250° C. 9. The method of claim 1 in which the plastic material of the thermoplastic film contains a plasticizer taken from the group consisting of a high polymer, a straight line long chain alcohol, a plastifying polymer, or a combination of these. 10. The method of claim 1 in which said thermoplastic film in step (g) has a cover layer in the area of said abutting edges, the viscosity of which at embossing temperature is lower than that of said thermoplastic film. 11. The method of claim 10 in which the cover layer is united to the thermoplastic film during embossing.