초록 ▼

A method of suppressing lead dust generated in the manufacture of pasted lead acid storage battery plates by coating the surface of a pasted battery plate with a solution or a suspension comprising ammonium sulfate, copolymer and water. The resultant water insoluble film is made porous by the simult

A method of suppressing lead dust generated in the manufacture of pasted lead acid storage battery plates by coating the surface of a pasted battery plate with a solution or a suspension comprising ammonium sulfate, copolymer and water. The resultant water insoluble film is made porous by the simultaneous evolution of ammonia gas produced during the coating process. The porous water insoluble film on the battery plate results in an electric storage battery with a lower internal resistance, than previously disclosed coatings and produces a battery with performance characteristics less inhibited than those made with previously disclosed coatings.

대표청구항 ▼

1. A method of reducing lead dust generated in the known manufacture of lead-acid storage batteries comprising pasting a supporting grid with a lead paste material and applying to the pasted grid a dust suppressing porous film forming amounts of a coating material comprising: ammonium sulfate; a

1. A method of reducing lead dust generated in the known manufacture of lead-acid storage batteries comprising pasting a supporting grid with a lead paste material and applying to the pasted grid a dust suppressing porous film forming amounts of a coating material comprising: ammonium sulfate; a copolymer emulsion; water; and drying said coating material to result in a water-insoluble porous film. 2. The method of claim 1 wherein the copolymeric emulsion comprises the following monomeric units: acrylate, styrene and acrylic acid; styrene and butadiene; alpha olefin monomers and vinyl acetate; butyl acrylate, acrylonitrile and methylolacrylamide; butyl acrylate, methacrylate and methacrylic acid. 3. The method of claim 1 wherein the copolymeric emulsion is selected from the group consisting of: Vinacryl 7172, Vinamul 6705, Dur O Cryl 620 and Stythemul DL 2519. 4. The method of claim 1 wherein the copolymeric emulsion is Vinacryl 7172. 5. The method of claim 1 wherein the copolymeric emulsion is Vinamul 6705. 6. The method of claim 1 wherein the copolymeric emulsion is Dur O Cryl 620. 7. The method of claim 1 wherein the copolymeric emulsion is Synthemul DL 2519. 8. A method of suppressing lead dust generated in the known manufacture of lead-acid storage batteries comprising applying to a pasted plate an aqueous dispersion of a copolymeric emulsion and ammonium sulfate; said ammonium sulfate reacting with the lead material of the pasted plate to produce gaseous ammonia; drying said pasted plate to result in a substantially lead dust-free pasted plate with a water insoluble copolymeric porous film thereon. 9. The method of claim 8 wherein the copolymeric emulsion comprises the following monomeric units: acrylate, styrene and acrylic acid; styrene and butadiene; alpha olefin monomers and vinyl acetate; butyl acrylate, acrylonitrile and methylolacrylamide; butyl acrylate, methacrylate and methacrylic acid. 10. The method of claim 8 wherein the copolymeric emulsion is selected from the group consisting of: Vinacryl 7172, Vinamul 6705, Dur O Cryl 620 and Synthemul DL 2519. 11. The method of claim 8 wherein the copolymeric emulsion is Vinacryl 7172. 12. The method of claim 8 wherein the copolymeric emulsion is Vinamul 6705. 13. The method of claim 8 wherein the copolymeric emulsion is Dur O Cryl 620. 14. The method of claim 8 wherein the copolymeric emulsion is Synthemul DL 2519. 15. A substantially dust free unformed leaded plate for lead acid storage batteries comprising a lead pasted supporting grid coated with a copolymeric water insoluble porous coating made porous by applying a suspension of copolymer emulsion, ammonium sulfate and water. 16. The leaded plate of claim 15 wherein the copolymeric emulsion comprises the following monomeric units: acrylate, styrene and acrylic acid; styrene and butadiene; alpha olefin monomers and vinyl acetate; butyl acrylate, acrylonitrile and methylolacrylamide; butyl acrylate, methacrylate and methacrylic acid. 17. The leaded plate of claim 15 wherein the copolymeric emulsion is selected from the group consisting of: Vinacryl 7172, Vinamul 6705, Dur O Cryl 620 and Synthemul DL 2519. 18. The leaded plate of claim 15 wherein the copolymeric emulsion is Vinacryl 7172. 19. The leaded plate of claim 15 wherein the copolymeric emulsion is Vinamul 6705. 20. The leaded plate of claim 15 wherein the copolymeric emulsion is Dur O Cryl 620. 21. The leaded plate of claim 15 wherein the copolymeric emulsion is Synthemul DL 2519. 22. A composition which reduces lead dust emanating from lead plates during the process of manufacturing lead-acid storage batteries comprising: ammonium sulfate; copolymeric emulsion wherein the monomeric units of the copolymeric emulsion are selected from the group consisting of: acrylate, styrene and acrylic acid; styrene and butadiene; alpha olefin monomers and vinyl acetate; butyl acrylate, acrylonitrile and methylolacrylamide; or butyl acrylate, methacrylate and methacrylic acid; and water. 23. The composition of claim 22 wherein the copolymeric emulsion is selected from the group consisting of Vinacryl 7172, Vinamul 6705, Dur O Cryl 620 and Synthemul DL 2519. 24. The composition of claim 22 wherein the copolymer emulsion comprises Vinacryl 7172. 25. The composition of claim 22 wherein the copolymer emulsion comprises Vinamul 6705. 26. The composition of claim 22 wherein the copolymer emulsion comprises Dur O Cryl 620. 27. The composition of claim 22 wherein the copolymer emulsion comprises Synthemul DL 2519.