초록 ▼

A method of determining tensile bond strength and lap shear strength betw a liner/insulation material and a propellant composition which is cured to portions of the liner/insulation material. The liner/insulation material is bonded to a propellant composition in a dogbone configuration by positioni

A method of determining tensile bond strength and lap shear strength betw a liner/insulation material and a propellant composition which is cured to portions of the liner/insulation material. The liner/insulation material is bonded to a propellant composition in a dogbone configuration by positioning a predetermined size of the liner/insulation material in a groove that is constructed in a mold in a transverse direction for a tensile bond strength specimen whereby the propellant is bonded to each side of the exposed liner/insulation material. The lap shear specimen is formed in a mold wherein a predetermined size of the liner/insulation material is longitudinally positioned in a groove that is constructed in a mold. The liner/insulation material is centered with a pair of spacers having about one-half of the length of the liner/insulation material to prevent a cast propellant composition from binding to the portion covered by the spacers but to permit the remaining portion of the liner/insulation material to be embedded and cured in the propellant composition that is cast and cured in the mold. After curing the tensile strength specimen and the lap shear specimen having the liner/material bonded to the cured propellant, each specimen is tested in an Instron testing machine to determine bond strength and bond characteristics of the test specimens by evaluating the strain at maximum stress, maximum strain, type of break and total area under the stress strain curve.

대표청구항 ▼

1. A method of preparing tensile strength and lap shear strength specimens for determining bond strength between a liner/insulation material and a cured hydroxyterminated polybutadiene propellant composition comprising: (i) preparing a liner/insulation material of a predetermined dimension and th

1. A method of preparing tensile strength and lap shear strength specimens for determining bond strength between a liner/insulation material and a cured hydroxyterminated polybutadiene propellant composition comprising: (i) preparing a liner/insulation material of a predetermined dimension and thickness and having flat surfaces facing in opposite directions; (ii) placing said liner/insulation material in a mold having a dogbone configuration and in a predetermined position in said mold; (iii) casting a curable hydroxyterminated polybutadiene propellant composition onto a portion of said oppositely facing surfaces of said liner/insulation material; (iv) curing said curable hydroxyterminated polybutadiene propellant composition to form a secure bond between said liner/insulation material oppositely facing surfaces and said cured propellant composition; and to provide a dogbone shaped specimen in which the hydroxyterminated polybutadiene is securely bonded to oppositely facing surfaces of said liner/insulation material; and (v) placing said tensile strength and lap shear strength specimens in a machine and determining bond strength between said liner/insulation material oppositely facing surfaces and said cured hydroxyterminated polybutadiene propellant composition. 2. The method of claim 1 wherein a first portion of said curable hydroxyterminated polybutadiene propellant composition is cast on a first portion of said surfaces of said liner/insulation material and a second portion of said curable hydroxyterminated polybutadiene propellant composition in cast on a second portion of said surfaces of said liner/insulation material. 3. The method of claim 1 wherein said curable hydroxyterminated polybutadiene propellant composition is cast in said mold and onto portions of said oppositely facing surfaces at opposite ends of said liner/insulation material with an intermediate portion of said oppositely facing surfaces having a discontinuance of propellant. 4. The method of claim 1 wherein a first portion of said curable hydroxyterminated polybutadiene propellant composition is cast on a first portion of said surfaces of said liner/insulation material and a second portion of said curable hydroxyterminated polybutadiene propellant composition is cast on a second portion of said surfaces of said liner/insulation material thereby providing a structure for testing the tensile strength of said curable hydroxyterminated polybutadiene propellant composition bonded to said liner/insulation material. 5. The method of claim 1 wherein said curable hydroxyterminated polybutadiene propellant composition is cast onto portions of said oppositely facing surfaces at opposite ends of said liner/insulation material with an intermediate portion of said oppositely facing surfaces having no propellant thereon thereby providing a structure for testing the lap shear strength of said curable hydroxyterminated polybutadiene propellant composition bonded to a liner/insulation material. 6. The method of claim 1 wherein prior to said casting of said curable hydroxyterminated polybutadiene propellant composition onto a portion of said surfaces of said liner/insulation material, said surfaces of said tensile and lap shear strength specimens are cleaned with methylene chloride, roughened with steel wool, passed under a magnet to remove residual steel wool, and rinsed with methylene chloride and dried to remove methylene chloride, and coated with a primer that is compatible with said tensile and lap shear strength specimens and said curable hydroxyterminated polybutadiene propellant composition and baked for about 30 minutes at 250° F.