초록 ▼

The scuff resistance of high-pressure laminated plastic is improved by incorporating in or very near the surface thereof, finely divided polyethylene wax having a particle size of about 1-25 microns and a melting point of preferably 220°-230°F. The wax is incorporated as part of an abrasion-resistan

The scuff resistance of high-pressure laminated plastic is improved by incorporating in or very near the surface thereof, finely divided polyethylene wax having a particle size of about 1-25 microns and a melting point of preferably 220°-230°F. The wax is incorporated as part of an abrasion-resistant coating mixture applied to the face of an unimpregnated decor paper sheet in an ultra-thin layer, which layer is dried at a temperature below the wax melting point and then impregnated with conventional melamine-formaldehyde resin. The impregnated sheet is placed onto a sheet of convention phenolic resin impregnated core sheets and consolidated in the conventional way under heat and pressure. During consolidation, the wax particles “bloom”, or migrate to the surface. The finished laminate surface has greatly improved scuff resistance.

대표청구항 ▼

In a decor sheet for use as a decorative facing sheet in the manufacture of abrasion-resistant decorative laminates, said decor sheet having thereon an ultra-thin facing layer comprising abrasion-resistant particles and sufficient binder material for said particles to bind said abrasion-resistant pa

In a decor sheet for use as a decorative facing sheet in the manufacture of abrasion-resistant decorative laminates, said decor sheet having thereon an ultra-thin facing layer comprising abrasion-resistant particles and sufficient binder material for said particles to bind said abrasion-resistant particles to the surface of said decor sheet, said decor sheet being imprenated with a thermosetting resin compatible with said binder material, the improvement wherein said ultra-thin layer also contains a solid, particulate lubricant, having a melting point of at least 140°F., in an amount sufficient such that, during use of the decor sheet to make decorative laminate, the particular lubricant melts and blooms to the surface thereby providing an abrasion-resistant laminate having simultaneously good clarity, excellent abrasion resistance and improved stain and scuff resistance, with the proviso that said solid lubricant is not an oxidized wax or a silicone resin. In a method of producing an abrasion-resistant decorative laminate from at least one backing layer and a thermosetting resin impregnated decor facing sheet, said laminate having enhanced abrasion resistance without an overlay layer, the method comprising providing a decorative facing sheet with an ultra-thin layer of abrasion-resistant particles and sufficient binder material for said particles to bind said particles to the sufface of said decor sheet and with an impregnant of a polyester or melamine-formaldehyde thermosetting resin; assembling said resin-impregnated and coated decor sheet over said backing layer; and subjecting said assembly to heat and pressure to consolidate said backing layer and said decor sheet to thereby provide said abrasion-resistant decorative laminate; the improvement wherein said ultra-thin wet layer further includes a solid, particulate lubricant, having a melting point of at least 140°F., in an amount sufficient such that during said consolidation step, the particulate lubriant melts and blooms to the surface thereby providing an abrasion-resistant laminate having simultaneously good clarity, excellent abrasion resistance and improved stain and scuff resistance, with the proviso that said solid lubricant is not an oxidized wax or a silicone resin; wherein said consolidation step is carried out at a temperature greater than the melting temperature of said solid, particulate lubricant. A method according to claim 18, wherein said decorative facing sheet is provided with said ultra-thin layer and with said impregnant by the steps of coating said decorative facing sheet with said ultra-thin layer of said abrasion-resistant particles and said binder material in a wet layer, drying said wet layer on said decor sheet at a temperature of about 170°-190°F. but less than the melting temperature of said solid, particulate lubricant and thereby providing a dried ultra-thin layer in which said abrasion-resistant particles are bound to the surface of said decor sheet by said binder material, and impregnating said coated decor sheet with said thermosetting resin impregnant; and wherein said solid particulate lubricant is a polyethylene wax having a particle size less than 30 microns, having a melting temperature of less than 260°F. and preferably 220°-230°F.