초록 ▼

Soft and tacky polymers can be ground at ambient temperature in the presence of a grinding aid in an atttrition mill having counter-rotating grinding elements operated above a minimum tip speed (170 m/sec) and at a throughput of more than about 90 kg/hr, the amount of grinding aid, which can be eith

Soft and tacky polymers can be ground at ambient temperature in the presence of a grinding aid in an atttrition mill having counter-rotating grinding elements operated above a minimum tip speed (170 m/sec) and at a throughput of more than about 90 kg/hr, the amount of grinding aid, which can be either organic or inorganic such as calcium carbonate, being about 5-20% based on the weight of polymer. The mill temperature is adjusted so that nearly all of the grinding aid is retained on the softened polymer particles, thus improving polymer flow and reducing to a minimum the amount of loose grinding aid to be disposed of. Air is drawn through the mill to serve as the material carrier medium and at the same time to cool the mill, if required. However, a portion of the exiting air can be recirculated to the mill to increase the temperature, if needed.

대표청구항 ▼

A process for grinding to a particle size of less than about 1 mm in diameter a soft and tacky polymeric material in the presence of a grinding aid in an attrition mill having counter-rotating grinding elements adjustably spaced apart, said process comprising the following steps: (a) introducing pol

A process for grinding to a particle size of less than about 1 mm in diameter a soft and tacky polymeric material in the presence of a grinding aid in an attrition mill having counter-rotating grinding elements adjustably spaced apart, said process comprising the following steps: (a) introducing polymer pellets and a grinding aid into the grinding area of an attrition mill having counter-rotating grinding elements operating at a combined tip speed of at least 170 m/sec, while passing air through the mill at a flow rate of at least about 350 m3 per kg of polymer throughput, the amount of grinding aid being about 5-20% based on the weight of the polymer; (b) grinding the polymer at a temperature such that the surfaces of polymer particles melt, thus allowing the grinding aid to well adhere thereto and minimizing the amount of grinding aid to be disposed of, at a mill setting such that about 1-40% of the polymer fed to the mill has a particle size of at least about 1 mm; (c) removing ground polymer from the grinding area by carrying it away with the stream of air; (d) separating ground polymer material having a smaller particle size of less than about 1 mm from the material having a larger particle size of at least 1 mm; (e) collecting the smaller particle size material and recycling the larger particle size material to the polymer fed to the mill, the recycled polymer being at a temperature such that it preheats the polymer fed to the mill to a selected temperature at or above ambient; (f) removing with the stream of air most loose grinding aid from the grinding area and, optionally, recovering it; and (g) when the temperature of recycled polymer is insufficient to preheat the polymer fed to the mill to the desired temperature, recycling a portion of the air exiting from the mill to the incoming air.