초록 ▼

A novel process is provided for producing prefoam type cellular concrete articles, which uses a foamed slurry (E) consisting essentially of an aqueous slurry (A) of a calcium silicate-based cement compound, an aqueous slurry (B) of a calcium aluminate-based cement compound, a specific setting retard

A novel process is provided for producing prefoam type cellular concrete articles, which uses a foamed slurry (E) consisting essentially of an aqueous slurry (A) of a calcium silicate-based cement compound, an aqueous slurry (B) of a calcium aluminate-based cement compound, a specific setting retarder (C), and an aqueous foamed liquid (D). The process is further characterized in that: (i) the foamed slurry (E) is cast and provided with hardened strength sufficient for demolding in 20 to 120 minutes after it has been poured into a mold; (ii) the demolded article is subjected to precuring under specific conditions of humidity, temperature and precuring time; and (iii) the molded article is then subjected to hydrothermal curing under high pressure.

대표청구항 ▼

In a process for producing cellular concrete which comprises mixing (A) an aqueous slurry of a cement compound comprising calcium silicate as a main hydraulic mineral component, (B) an aqueous slurry of a rapid-hardening cement compound comprising a calcium aluminate as a main hydraulic mineral comp

In a process for producing cellular concrete which comprises mixing (A) an aqueous slurry of a cement compound comprising calcium silicate as a main hydraulic mineral component, (B) an aqueous slurry of a rapid-hardening cement compound comprising a calcium aluminate as a main hydraulic mineral component, (C) a setting retarder, and (D) an aqueous foamed liquid to obtain a foamed slurry, and (D) an aqueous foamed liquid to obtain a foamed slurry (E) of a rapid-hardening cement compound having an apparent specific gravity of 0.4 to 1.2, casting the resulting mixture in a mold, and subjecting the resulting molded article, after demolding, to high-temperature and high pressure hydrothermal curing to produce a cellular concrete article, the improvement which comprises conducting the process under the following conditions (1) through (4): (1) the setting retarder (C) is at least one member selected from the group consisting of (a) an alkali metal citrate, (b) an alkali metal tartarate, (c) citric acid and an alkali metal carbonate or bicarbonate, and (d) tartaric acid and an alkali metal carbonate or bicarbonate; (2) the amount of setting retarder is such that strength sufficient for demolding without deformation is developed in 20 to 120 minutes after pouring the foamed slurry (e) into the mold, and the product is then demolded; (3) the resulting demolded article is subjected to precuring which comprises maintaining it in a warm wet state under atmospheric pressure under the conditions of temperature and period of time corresponding to the region surrounded by the curves A and B in the attached drawing, whereby at least a part of the initial strength dependent upon the hydration of the calcium aluminate from the slurry (B) in the molded article is replaced by the strength imparted by the hydration of the hydraulic cement compound from the slurry (A); and (4) the molded article is then subjected to high-temperature and high-pressure hydrothermal curing at 150°to 190°C.