초록 ▼

A polymer in the form of particles is water-insoluble and water-sellable, containing carboxyl or carboxylate groups. It has a physiological saline absorption quantity of 40 to 90 grams per one gram of the polymer, a physiological saline absorption rate of at least 8 ml per 0.3 gram of the polymer, a

A polymer in the form of particles is water-insoluble and water-sellable, containing carboxyl or carboxylate groups. It has a physiological saline absorption quantity of 40 to 90 grams per one gram of the polymer, a physiological saline absorption rate of at least 8 ml per 0.3 gram of the polymer, a gel strength of 33 to 200 g/cm2 when it has been swollen to saturation with ion-exchange water. It is useful as an absorbent in a sanitary article.

대표청구항 ▼

A process for preparing a water-insoluble, water-swellable polymer, which comprises the steps of: dispersing (1) an aqueous solution of a water-soluble, ethylenically unsaturated monomer having a carboxyl or carboxylate group in the molecule, in (2) a hydrophobic organic liquid dispersion medium to

A process for preparing a water-insoluble, water-swellable polymer, which comprises the steps of: dispersing (1) an aqueous solution of a water-soluble, ethylenically unsaturated monomer having a carboxyl or carboxylate group in the molecule, in (2) a hydrophobic organic liquid dispersion medium to form a water-in-oil suspension, said suspension also containing a protective colloid selected from the group consisting of cellulose esters and cellulose ethers, said protective colloid being insoluble or sparingly soluble in said dispersion medium at room temperature; then polymerizing said monomer under water-in-oil suspension polymerization conditions, in the presence of a water-soluble radical polymerization initiator, at an elevated polymerization temperature, said protective colloid being soluble in said dispersion medium at said elevated polymerization temperature, whereby to form particles of a hydrophilic polymer dispersed in said liquid dispersion medium; then removing water from said dispersion so that said hydrophilic polymer has a water content of from 10 to 40 percent by weight, then mixing said dispersion in which said hydrophilic polymer has a water content of from 10 to 40 percent by weight, with a crosslinking agent containing at least 2 functional groups reactive with carboxyl and carboxylate groups, under conditions effective to crosslink said polymer and to provide a higher crosslinking density on the surfaces of said polymer particles than in the interiors of said polymer particles; and then removing said dispersion medium to obtain said polymer particles.