초록 ▼

A process is disclosed for recovering chromium from a chromium bearing material containing cobalt, molybdenum, and tungsten. The process involves roasting the material and alkali metal compound at a temperature of at least about 400°C. for a sufficient time to react the alkali metal compound with th

A process is disclosed for recovering chromium from a chromium bearing material containing cobalt, molybdenum, and tungsten. The process involves roasting the material and alkali metal compound at a temperature of at least about 400°C. for a sufficient time to react the alkali metal compound with the material and form a reacted mixture containing essentially all of the chromium, molybdenum, and tungsten as alkali salts. The reacted mixture is water leached to dissolve the alkali salts and form a leach solution containing essentially all of the chromium, molybdenum, and tungsten, and a leach solid containing essentially all of the cobalt. After separation of the leach solution from the leach solid, the pH of the leach solution is adjusted to from about 0.5 to about 3.0 with an acid and a sufficient amount of a reducing agent is added to reduce essentially all of the chromium to the trivalent state. A precipitating agent is added to precipitate essentially all of the molybdenum and tungsten values while leaving essentially all of the reduced chromium values in the mother liquor, while the pH is maintained at from about 0.5 to about 3.0. The precipitate is separated from the mother liquor. A sufficient amount of ammonium sulfate is added to this mother liquor to precipitate essentially all of the chromium contained therein.

대표청구항 ▼

A process for recovering chromium from a chromium bearing material containing cobalt, molybdenum, and tungsten, said process comprising: (a) roasting a mixture of said material and an alkali metal compound at a temperature of at least about 400°C. for a sufficient time to react said alkali metal com

A process for recovering chromium from a chromium bearing material containing cobalt, molybdenum, and tungsten, said process comprising: (a) roasting a mixture of said material and an alkali metal compound at a temperature of at least about 400°C. for a sufficient time to react said alkali metal compound with said material and form a reacted mixture containing essentially all of said chromium, molybdenum and tungsten as alkali salts; (b) water leaching said reacted mixture to dissolve said alkali salts and form a leach solution containing essentially all of said chromium, said molybdenum, and said tungsten and a leach solid containing essentially all of said cobalt; (c) separating said leach solution from said leach solid; (d) adjusting the pH of said leach solution to from about 0.5 to about 3.0 with an acid; (e) adding to the resulting pH adjusted leach solution a sufficient amount of a reducing agent to reduce essentially all of said chromium to the trivalent state, and a sufficient amount of a precipitating agent to precipitate essentially all of the molybdenum and tungsten values while leaving essentially all of the resulting reduced chromium values in the resulting mother liquor, while maintaining the pH of the resulting reducing agent and precipitating agent treated leach solution at from about 0.5 to about 3.0; (f) separating the precipitate of molybdenum and tungsten from the resulting chromium containing mother liquor; (g) adding to said chromium containing mother liquor a sufficient amount of ammonium sulfate to form a precipitate containing essentially all of the chromium which was in said chromium containing mother liquor; and (h) separating the resulting chromium containing precipitate from the resulting mother liquor.