The present invention provides a gun capable of operating at relatively higher temperatures. The barrel of the gun is made up of at least two layers. The inner layer is of a refractory material which may be a metal refractory or a non-metal refractory. The liner is bonded to an outer jacket material

The present invention provides a gun capable of operating at relatively higher temperatures. The barrel of the gun is made up of at least two layers. The inner layer is of a refractory material which may be a metal refractory or a non-metal refractory. The liner is bonded to an outer jacket material formed of an alloy of nickel, aluminum and molybdenum. The coefficient of expansion of the liner and of the jacket are relatively low so that the gun does not expand extensively when heated by intensive use. The jacket metal is of higher strength at elevated temperature than is the conventional gun barrel steel.

대표청구항 ▼

The method of forming a gun barrel having a rifled bore and capable of high rates of fire at high energy which comprises, providing a mandrel conforming to the bore of the barrel, low pressure plasma depositing on said mandrel a liner of refractory material, low pressure plasma depositing on said re

The method of forming a gun barrel having a rifled bore and capable of high rates of fire at high energy which comprises, providing a mandrel conforming to the bore of the barrel, low pressure plasma depositing on said mandrel a liner of refractory material, low pressure plasma depositing on said refractory liner a barrel jacket of an alloy of nickel, aluminum and molybdenum, said alloy having a composition falling within the area enclosed by curve I of FIG. 5, and said alloy having a 0.2% yield strength in excess of 140 ksi at temperatures up to 1200°F.