초록 ▼

The powder of hexagonal boron nitride is prepared by heat-treating a powdery mixture composed of an oxygen-containing boron compound, e.g. boric acid, and a nitrogen compound, e.g. dicyandiamide and melamine, with admixture of minor amounts of a carbonaceous powder, e.g. carbon black, and/or borax.

The powder of hexagonal boron nitride is prepared by heat-treating a powdery mixture composed of an oxygen-containing boron compound, e.g. boric acid, and a nitrogen compound, e.g. dicyandiamide and melamine, with admixture of minor amounts of a carbonaceous powder, e.g. carbon black, and/or borax. Further, an alkaline earth metal compound such as calcium carbonate is added either to the powdery mixture of the starting materials before the heat treatment or to the powder after the heat treatment. The h-BN powder has excellent sinterability so that sintered bodies of boron nitride having a high density and high bending strength can readily be prepared by use of a hot press.

대표청구항 ▼

A powder of hexagonal boron nitride with excellent sinterability having a purity of at least 95% by weight as boron nitride and containing an alkaline earth metal compound in an amount from 0.0001 to 0.1 mole calculated as alkaline earth metal per mole of boron, of which the crystallites (Lc) have a

A powder of hexagonal boron nitride with excellent sinterability having a purity of at least 95% by weight as boron nitride and containing an alkaline earth metal compound in an amount from 0.0001 to 0.1 mole calculated as alkaline earth metal per mole of boron, of which the crystallites (Lc) have a size in the range from 8 to 50 nm. A method for the preparation of a powder of hexagonal boron nitride having excellent sinterability which comprises the steps of: (a) mixing boric acid, dehydrated boric acid, ammonium borate and a nitrogen compound selected from the group consisting of urea, melamine, dicyandiamide, cyanuric acid and ammonium chloride to produce a powdery mixture; (b) admixing the powdery mixture with 0.005 to 0.1 moles of a carbonaceous powder calculated as carbon per mole of boron in the powdery mixture and 2.5 to 30% by weight of borax or anhydrous borax calculated as anhydrous borax based on the boric acid, dehydrated boric acid and ammonium borate in the powdery mixture; and (c) subjecting the powdery mixture to a heat treatment in a non-oxidizing atmosphere.