초록 ▼

A process and apparatus is provided for making a rubber-like product from rubber scrap, such as recycled tire scrap. The process includes mixing the rubber scrap with from 1 percent to 15 percent, with respect to the weight of the rubber scrap, of added sulphur, and applying a pressure thereto of ab

A process and apparatus is provided for making a rubber-like product from rubber scrap, such as recycled tire scrap. The process includes mixing the rubber scrap with from 1 percent to 15 percent, with respect to the weight of the rubber scrap, of added sulphur, and applying a pressure thereto of about 1000 to 3000 pounds per square inch for 1 to 10 minutes at a temperature of from about 250 degrees F. to about 450 degrees F. In addition, 1 to 8 percent, with respect to the weight of the rubber scrap, of antioxidants and antiozonants are added to the mixture of rubber scrap and sulphur. The sulphur is free sulphur. Derivative sulphur compounds, or like vulcanizing agents, can be added in place of the free sulphur of about 1 to 45 percent of the weight of the rubber scrap. The rubber scrap is buffing of recycled tire rubber, or powder made from recycled tire rubber. An apparatus for carrying out the process is also provided. The apparatus includes a heavy duty mixer for making the mixture of the rubber scrap and sulphur and antioxidants and antiozonants. The apparatus also includes a compression molding and heating apparatus for applying the pressure and temperature to the mixture. The process is particularly suitable for making roofing products.

대표청구항 ▼

A process of making a roofing product, such as roll roofing, tiles, shakes, slates, walkway pads, and the like, including the steps of: a. providing a selected weight of rubber scrap; b. mixing the selected weight of rubber scrap with from 1 percent by 15 percent with respect to the weight of the ru

A process of making a roofing product, such as roll roofing, tiles, shakes, slates, walkway pads, and the like, including the steps of: a. providing a selected weight of rubber scrap; b. mixing the selected weight of rubber scrap with from 1 percent by 15 percent with respect to the weight of the rubber scrap of added sulphur to form a mixture; c. feeding the mixture into a gap of selective thickness disposed between a pair of compression rotary cylinders to form a continuous roofing product sheet; d. applying a pressure from the rollers to the sheet of about 1000 to 3000 pounds per square inch for 1 to 10 minutes while feeding the mixture; and e. applying a temperature of from about 250 degrees F. to about 450 degrees F. to the mixture and the sheet while feeding the mixture.