초록 ▼

A process for producing a porous ceramic filter for use in the filtering of particulates from diesel exhaust gases, and the filter so produced, in which a foamable ceramic composition based upon an aluminosilicate hydrogel binder is expanded into a self-supporting, open-celled porous body of desired

A process for producing a porous ceramic filter for use in the filtering of particulates from diesel exhaust gases, and the filter so produced, in which a foamable ceramic composition based upon an aluminosilicate hydrogel binder is expanded into a self-supporting, open-celled porous body of desired shape by virtue of in situ reaction between components of the composition, and thereafter treated to substantially reduce its alkali metal content and fired to produce ceramic bonds, the process further preferably providing on the intended outlet surface of the filter a thin porous ceramic membrane layer whose pores have an average diameter less than that of the pores within and at other surfaces of the ceramic filter.

대표청구항 ▼

A process for producing a porous refractory ceramic filter for use in the filtering of particulates from diesel exhaust gases, said filter having an inlet surface for receipt of diesel exhaust gases and an outlet surface for discharge of diesel exhaust gases which have traversed through said filter,

A process for producing a porous refractory ceramic filter for use in the filtering of particulates from diesel exhaust gases, said filter having an inlet surface for receipt of diesel exhaust gases and an outlet surface for discharge of diesel exhaust gases which have traversed through said filter, comprising the steps of: (a) providing a foamable ceramic composition comprised of an aqueous admixture of (1) an alkali metal silicate and an alkali metal aluminate, each in an amount effective to form therebetween an aluminosilicate hydrogel which binds all components of said composition, after foaming, into a self-supporting body in the desired shape of said filter; (2) refractory ceramic materials; (3) metal powder in an amount effective to react with alkali metal in said composition and generate as a product hydrogen gas in an amount effective to bring about foaming and expansion of said foamable ceramic composition; (4) a surfactant in an amount effective to form from said hydrogen gas small bubbles which provide a predominantly open-celled porosity in the foamed and expanded foamable ceramic composition, and (5) a gel strengthening and viscosity-modifying magnet in an amount effective to reduce the viscosity of said foamable ceramic composition as compared to the same composition without said gel-strengthening and viscosity-modifying agent; (b) introducing a quantity of said foamable ceramic composition into a shape-defining area for a time sufficient to permit reaction among the components of said composition to produce a foamed, porous aluminosilicate hydrogel-bound, self-supporting ceramic precursor of predominantly open-celled porosity in the shape of said shape-defining area; (c) removing said self-supporting precursor from said shape-defining area; (d) contacting said self-supporting precursor with water for a time effective to remove therefrom leachable alkali metal compounds; (e) thereafter contacting said self-supporting precursor with a dilute solution of non-alkali metal inorganic salt to effect substantially complete exchange of the ion of said non-alkali metal inorganic salt for the alkali metal ion of remaining alkali metal compounds in said self-supporting precursor; and (f) thereafter firing said self-supporting precursor to form ceramic bonds therein and produce said porous refractory ceramic filter having a predominantly open-celled porosity.