초록 ▼

A two-part for reinforcing a hollow strucutral members and its method of use are provided. A method of reinforcing a structural member having a hollow cavity comprises the steps of preparing a first dough which includes a thermal setting resin, a first filler and unexpanded, thermally-expandable mic

A two-part for reinforcing a hollow strucutral members and its method of use are provided. A method of reinforcing a structural member having a hollow cavity comprises the steps of preparing a first dough which includes a thermal setting resin, a first filler and unexpanded, thermally-expandable microspheres. A further step includes preparing a second dough which includes a curing agent, a colorant and a second filler. The curing agent is compatible with the thermosetting resin to promoter cross-linking of the thermosetting resin upon contact with the curing agent. The hollow structural member may be preheated to enhance the rate at whcih the thermosetting resin cross-links. The two dough are blended together until a reactive third dough of substantially uniform mixture is formed. The uniformity of the blending is confirmed when the reactive third dough attains a uniform color intermediate the color between the colors of the first and second doughs. The blended reactive dough is then packed into the cavity of the cleaned structural member. The cavity is then preferably closed with a closure plate. As the curing agent promotes the cross-linking reaction of the thermosetting resin, the exothermic reaction generates heat which is transferred to the unexpanded, thermally-expandable microspheres, causing the microspheres to expand. The expansion of the microspheres causes the reactie dough to rise, substantially filling the cavity. As the reactive dough cures, it bonds rigidly to the surfaces whcih it contacts. The reactive dough is allowed to fully cure, whereupon a solid lightweight reinforcement member rigidly bonded to the structural member is formed.

대표청구항 ▼

A method of preparing a composition for use in reinforcing a hollow structural member comprising the steps of: combining a liquid thermosetting resin, a first filler and unexpanded, thermally-expandable microspheres; blending said combination of said thermosetting resin, said first filler and said u

A method of preparing a composition for use in reinforcing a hollow structural member comprising the steps of: combining a liquid thermosetting resin, a first filler and unexpanded, thermally-expandable microspheres; blending said combination of said thermosetting resin, said first filler and said unexpanded, thermally-expandable microspheres to form a first dough; the first dough including from about 5 to 99 percent by weight of the thermosetting resin, from about 0.1 to about 20 percent by weight of the unexpanded thermally-expandable microspheres and from about 0.5 to about 90 percent by weight of the first filler to provide a doughy consistency to the first dough; combining a liquid curing agent, a colorant, and a second filler; and blending said combination of said liquid curing agent, said colorant and said second filler to form a second dough; the second dough including from about 10 to about 90 percent by weight of the curing agent adapted to promote cross-linking polymerization of the thermosetting resin in an exothermic reaction, and from about 0.5 to about 90 percent by weight of the second filler to provide a doughy consistency to the second dough. A method of reinforcing a structural member having a cavity comprising the steps of: preparing a first dough which includes a thermosetting resin, a first filler and unexpanded, thermally-expandable microspheres; the first dough including from about 5 to 99 percent by weight of the thermosetting resin, from about 0.1 to about 20 percent by weight of the thermally-expandable microspheres and from about 0.5 to about 90 percent by weight of the first filler to provide a doughy consistency to the first dough; preparing a second dough which includes a curing agent, a colorant and a second filler; the second dough including from about 10 to about 90 percent by weight of the curing agent adapted to promote cross-linking polymerization of the thermosetting resin in an exothermic reaction, and from about 0.5 to about 90 percent by weight of the second filler to provide a doughy consistency to the second dough; blending together said first dough and said second dough to form a reactive third dough; and packing said reactive third dough in said cavity of said structural member; wherein said curing agent promotes the cross-linking of said thermosetting resin in a reaction which releases heat, wherein said heat of said reaction causes said unexpanded, thermally-expandable microspheres to expand such that said reactive dough expands, and wherein said cross-linking of said thermosetting resin continues until said thermosetting resin substantially cures to form a rigid body which adheres to and reinforces said structural member.