A method of manufacturing high-zirconium getters that involves hydrogen pulverization of an entire alloy ingot or ingot pieces. The method offers distinct advantages over techniques that use mechanical means of powder production. The method is useful especially in the manufacture of tough porous get

A method of manufacturing high-zirconium getters that involves hydrogen pulverization of an entire alloy ingot or ingot pieces. The method offers distinct advantages over techniques that use mechanical means of powder production. The method is useful especially in the manufacture of tough porous getters, of high Zr-content Zr-V alloys that have minor additions of elements such as Fe, Ni, Mn and/or Al.

대표청구항 ▼

A tough porous non-evaporable getter product produced according to steps as follows: providing a solid alloy body of Zr, V and E wherein E consists of more than one of Fe, Ni, Mn and Al such that the proportions of each species are in weight percent E from 4 to 5, V from 10 to 16 and Zr balance to

A tough porous non-evaporable getter product produced according to steps as follows: providing a solid alloy body of Zr, V and E wherein E consists of more than one of Fe, Ni, Mn and Al such that the proportions of each species are in weight percent E from 4 to 5, V from 10 to 16 and Zr balance to make 100 and from 79 to 86, introducing the body into a chamber and removing the air therefrom, charging the body with hydrogen for hydride formation to induce spontaneous pulverization of the body into the hydride powder and/or granules, forming the powder and/or granules into a desired getter shape, and sintering the shape under a dynamic vacuum or flowing inert gas at a temperature in the range of 900°to 1200°C. but below its melting temperature.