초록 ▼

A high temperature film wrapping is used to wrap thermoplastic materials before they are molded. The thermoplastic material can then be molded by applying heat and pressure and the resulting thermoplastic material will contain reduced cracks and voids compared with thermoplastic materials molded wit

A high temperature film wrapping is used to wrap thermoplastic materials before they are molded. The thermoplastic material can then be molded by applying heat and pressure and the resulting thermoplastic material will contain reduced cracks and voids compared with thermoplastic materials molded without the wrapping.

대표청구항 ▼

1. A process comprising: (a) wrapping a sleeve material around at least one thermoplastic material to form a sleeve-wrapped material; (b) placing said sleeve-wrapped material in a positive pressure mold to form a mold assembly; (c) heating said mold assembly so that said thermoplastic material

1. A process comprising: (a) wrapping a sleeve material around at least one thermoplastic material to form a sleeve-wrapped material; (b) placing said sleeve-wrapped material in a positive pressure mold to form a mold assembly; (c) heating said mold assembly so that said thermoplastic material is heated to a molten state; (d) compressing said mold assembly in a press so that said sleeve-wrapped material is formed into a formed material; (e) cooling said formed material to harden said formed material; and (f) removing said sleeve material from said formed material. 2. A process according to claim 1 wherein said formed material is cooled in said cooling step (e) under pressure. 3. A process according to claim 1 wherein said compressing in step (d) is at a pressure in the range of from contact pressure to about 2.76 MPa (400 psi). 4. A process according to claim 6 wherein said compressing in step (d) is at a pressure in the range of from contact pressure to 2.09 MPa (300 psi). 5. A process in accordance with claim 1 wherein said sleeve-wrapped material is heated in said heating step (c) to a temperature under a first pressure and said compressing in step (c) occurs at about said temperature and at a second pressure higher than said first pressure. 6. A process according to claim 5 wherein said first pressure is in the range of from about contact pressure to about 0.34 MPa (50 psi), said second pressure is in the range of from about 1.03 MPa (150 psi) to about 2.76 MPa (400 psi) and said temperature is sufficient to maintain the thermoplastic in an essentially molten state. 7. A process according to claim 1 wherein said sleeve material is selected from the group consisting of a polyimide film, polytetrafluoroethylene release cloth, and glass cloth fabric. 8. A process according to claim 1 further comprising coating said sleeve material with a releasing agent. 9. A process according to claim 8 wherein said releasing agent is a silicone oil or silicone wax. 10. A process according to claim 1 wherein said at least one thermoplastic material is selected from the group consisting of poly(arylene sulfides) and mixtures thereof. 11. A process according to claim 1 wherein said at least one thermoplastic material is reinforced with at least one fiber. 12. A process according to claim 11 wherein said at least one fiber is selected from the group consisting of glass, quartz, aramid, metal, ceramic and carbon fibers and mixtures of two or more thereof. 13. A process according to claim 1 further comprising placing at least one insert with said at least one thermoplastic material before said wrapping step (a) and wherein said wrapping step (a) comprises wrapping a sleeve material around said at least one insert and said at least one thermoplastic material. 14. A process according to claim 1 wherein: said sleeve-wrapped material is heated in said heating step (c) to a temperature under a first pressure; said compression step (d) is performed in said positive pressure mold and occurs at about said temperature and at a second pressure higher than said first pressure; and said formed material is cooled in said cooling step (e) under a third pressure. 15. A process according to claim 14, wherein: said sleeve material is a polyimide film; said at least one thermoplastic material is poly(phenylene sulfide); said first pressure is in the range of from about contact pressure to about 0.34 MPa (50 psi); said second pressure is in the range of from about 1.03 MPa (150 psi) to about 2.76 MPa (400 psi); said temperature is in the range of from about 288° C. (550° F.) to about 371° C. (700° F.); and said third pressure is about the same as said second pressure. 16. A process according to claim 1 wherein said step (a) comprises wrapping said sleeve material around at least one thermoplastic material so that at least one end of the sleeve is open.