초록 ▼

A mild hydrocracking process for the hydrodemetallation (HDM), hydrodesulfurization (HDS) and hydroconversion (HC) of hydrocarbon feedstocks such as residuum feedstocks which provides increased conversion of the 1000° F.+ hydrocarbon fraction to the 1000° F.- fraction and increased yields of middle

A mild hydrocracking process for the hydrodemetallation (HDM), hydrodesulfurization (HDS) and hydroconversion (HC) of hydrocarbon feedstocks such as residuum feedstocks which provides increased conversion of the 1000° F.+ hydrocarbon fraction to the 1000° F.- fraction and increased yields of middle distillates is disclosed. The process utilizes a catalyst comprising about 2.0 to about 6.0 wt. % of an oxide of a Group VIII metal, about 12.0 to about 25.0 wt. % of an oxide of molybdenum and 0 to about 3.0 wt. % of an oxide of phosphorus supported on a porous alumina support containing about 4.0 to about 30 wt. % of silica.

대표청구항 ▼

1. A process for mild hydrocracking of a hydrocarbon feedstock having a substantial proportion of components boiling below about 1000° F., said process comprising contacting said hydrocarbon feedstock under conditions of elevated temperature and a hydrogen pressure of less than about 1500 psig with

1. A process for mild hydrocracking of a hydrocarbon feedstock having a substantial proportion of components boiling below about 1000° F., said process comprising contacting said hydrocarbon feedstock under conditions of elevated temperature and a hydrogen pressure of less than about 1500 psig with a particulate catalyst comprising about 2.0 to about 6.0 wt. % of an oxide of a Group VIII metal; about 12.0 to about 25.0 wt. % of an oxide of molybdenum and 0 to about 3.0 wt. % of an oxide of phosphorus all supported on a porous alumina support containing about 10.0 to about 25.0 wt. %, based on the weight of the support, of silica, in such a manner that the molybdenum gradient of the catalyst has a value between about 1 and about 10, said conditions being such as to yield about a 10 to about a 60 Vol % conversion of the hydrocarbon feedstock boiling above 650° F. to hydrocarbon products boiling at or below 650° F., and wherein the catalyst is further characterized by having a total surface area of about 150 to about 250 m 2 /g and a total pore volume of about 0.75 to about 0.92 cc/g with a pore diameter distribution such that pores having diameters of less than 100 .ANG. constitute about 20.0 to about 40.0%, pores having diameters of 100-160 .ANG. constitute 28.4 to 34.1%, pores having diameters of less than 160 .ANG. constitute about 50.0 to about 70.0%, pores having diameters of greater than 160 .ANG. constitute about 30.0 to about 50.0%, of the total pore volume of the said catalyst and macropores having diameters greater than 250 .ANG. constitute about 25.0 to about 40.0% of the total pore volume of said catalyst. 2. The process of claim 1 wherein the said catalyst contains about 16 to about 25 wt. % of silica. 3. The process of claim 1 wherein in the said catalyst the said Group VIII metal is nickel. 4. The process of claim 1 wherein the said catalyst comprises about 2.5 to about 3.5 wt. % NiO and about 12.0 to about 18.0 wt. % MoO 3 supported on the said porous alumina support. 5. The process of claim 1 wherein the said hydrocarbon feedstock is contacted with said catalyst in a fixed bed reactor. 6. The process of claim 1 wherein the said hydrocarbon feedstock is contacted with said catalyst in a single ebullated bed reactor. 7. The process of claim 1 wherein the said hydrocarbon feed is contacted with said catalyst in a series of 2-5 ebullated bed reactors. 8. The process of claim 1 wherein the said hydrocarbon feed is contacted with said catalyst in a series of 2-5 continuous stirred tank reactors. 9. The process of claim 1 wherein the said hydrocarbon feed is contacted with said catalyst in a single continuous stirred tank reactor.