초록 ▼

The invention relates to the use of polymeric foam materials for insulation. These polymeric foams are prepared by polymerization of certain water-in-oil emulsions having a relatively high ratio of water phase to oil phase, commonly known in the art as high internal phase emulstions, or “HIPEs.”The

The invention relates to the use of polymeric foam materials for insulation. These polymeric foams are prepared by polymerization of certain water-in-oil emulsions having a relatively high ratio of water phase to oil phase, commonly known in the art as high internal phase emulstions, or “HIPEs.”The HIPE-derived foam materials used in the present invention comprise a generally hydrophobic, flexible, semi-flexible, or rigid nonionic polymeric foam structure of interconnected open-cells. These foam structures have: A) a specific surface area per foam volume of at least about 0.01 m2/cc; B) a density of less than about 0.05 g/cc; and C) a glass transition temperature (Tg) of between about -20°and 90°C. The foams can be used as thermal, acoustic, and/or mechanical insulation materials. In a preferred embodiment, the foams used can be prepared, packaged, and shipped in a compressed, high density state and will “spring back”upon activation (e.g. heat) to the original density of the foam.

대표청구항 ▼

A method of insulating an object, comprising locating a polymeric foam material proximate to the object, wherein the polymeric foam material has: A) s specific surface area per foam volume of at least about 0.01 m/cc; B) a dry density of less than about 0.05 g/cc; and C) a glass transition temperatu

A method of insulating an object, comprising locating a polymeric foam material proximate to the object, wherein the polymeric foam material has: A) s specific surface area per foam volume of at least about 0.01 m/cc; B) a dry density of less than about 0.05 g/cc; and C) a glass transition temperature (Tg) of between about -20°and 90°C.; and wherein the polymeric foam material is prepared by the process comprising the steps of (A) forming a water-in-oil emulsion at a temperature of about 30°C. or higher and under low shear mixing from: (1) an oil phase comprising: (a) from about 80% to about 98% by weight of a monomer component capable of forming a copolymer having a Tg value of from about -20°C. to about 90°C., said monomer component comprising: (i) from about 10% to about 70% by weight of a substantially water-insoluble, monofunctional monomer capable of forming a homopolymer having a Tg of about 35°C. or less; (ii) from about 10% to about 70% by weight of a substantially water-insoluble, monofunctional comonomer capable of imparting toughness about equivalent to that provided by styrene; (iii) from about 2% to about 50% of a first substantially water-insoluble, polyfunctional crosslinking agent selected from the group consisting of divinyl benzene and analogs thereof; and (iv) from about 0% to about 15% of a second substantially water-insoluble, polyfunctional crosslinking agent selected from the group consisting of diacrylates of diols and analogs thereof; and (b) from about 2% to about 20% by weight of an emulsifier component which is soluble in the oil phase and which is suitable for forming a stable water-in-oil emulsion; (2) a water phase comprising from about 0.1% to about 20% by weight of a water-soluble electrolyte; and (3) a volume to weight ratio of water phase to oil phase in the range of from about 12:1 to about 250:1; and (B) polymerizing the monomer component in the oil phase of the water-in-oil emulsion to form the polymeric foam material.