초록 ▼

Damage-tolerant, continuous fiber ceramic matrix composites are fabricated to fill the space between the fibers with a powder. The powder particles are heat treated to form a porous framework without shrinkage, which is then strengthened with an inorganic synthesized from a precursor in solution. Hi

Damage-tolerant, continuous fiber ceramic matrix composites are fabricated to fill the space between the fibers with a powder. The powder particles are heat treated to form a porous framework without shrinkage, which is then strengthened with an inorganic synthesized from a precursor in solution. High particle packing densities is achieved within the fiber preform using a small particle-to-fiber diameter ratio. Filling the interstices with a powder increases the composite density and also limits the size of the crack-like voids within the matrix. The ceramic matrix composite (CMC) has mechanical characteristics similar to those found in wood. It is also affordable and inherently oxidation resistant. The composite is characterized by a heterogeneous distribution of fibers within a porous matrix having a homogeneous, fine porosity. A residual stress from thermal expansion mismatch of the matrix and fibers is created in the composite. The illustrated embodiment uses Al.sub.2 O.sub.3 fibers with either mullite or Si.sub.3 N.sub.4 matrices.

대표청구항 ▼

[ We claim:] [1.] A ceramic matrix composite comprising:a plurality of alumina fibers, not precoated and having an average diameter of 40 .mu.m of less; anda porous matrix impregnated about said fibers comprising:background mullite particles having an average diameter smaller than that of the alumin

[ We claim:] [1.] A ceramic matrix composite comprising:a plurality of alumina fibers, not precoated and having an average diameter of 40 .mu.m of less; anda porous matrix impregnated about said fibers comprising:background mullite particles having an average diameter smaller than that of the alumina fibers so that a ratio between particle diameter and fiber diameter is less than 0.1;packing voids between the mullite particles; andinterstitial mullite binding particle to particle and particle to fiber forming a nonshrinking matrix through which cracks propagate without entering the fibers when the ceramic matrix composite fails.