초록 ▼

Proposed is a method for the preparation of an aqueous slurry of calcium carbonate particles suitable as a base pigment in the preparation of a paper coating composition having excellent water retentivity and high solid concentration with good flowability, which contains precipitated and ground calc

Proposed is a method for the preparation of an aqueous slurry of calcium carbonate particles suitable as a base pigment in the preparation of a paper coating composition having excellent water retentivity and high solid concentration with good flowability, which contains precipitated and ground calcium carbonate particles in combination in a specified weight proportion and characterized by several parameters. The aqueous slurry is prepared in a process comprising the steps of: (a) subjecting an aqueous slurry or wet cake containing a specified amount of specific precipitated calcium carbonate particles to a primary dispersing treatment using a mixer to a specified extent; (b) admixing the aqueous slurry with a specified amount of specific ground calcium carbonate particles; (c) subjecting the aqueous slurry to a secondary dispersing treatment using a mixer to a specified extent; and (d) subjecting the aqueous slurry to a tertiary dispersing treatment using a sand grinder to a specified extent.

대표청구항 ▼

[ What is claimed is:] [1.] A method for the preparation of an aqueous slurry of calcium carbonate particles which comprises the steps of:(a) subjecting an aqueous slurry or a dehydrated wet cake of precipitated calcium carbonate particles containing an admixture of a viscosity-reducing agent having

[ What is claimed is:] [1.] A method for the preparation of an aqueous slurry of calcium carbonate particles which comprises the steps of:(a) subjecting an aqueous slurry or a dehydrated wet cake of precipitated calcium carbonate particles containing an admixture of a viscosity-reducing agent having a solid concentration in the range from 25 to 75% by weight to a primary dispersing treatment by using a mixer so that the calcium carbonate particles have a median diameter in the range from 0.2 to 3.0 Jim and the slurry has a viscosity not exceeding 1000 centipoise at 25.degree. C.;(b) admixing the aqueous slurry of (a) with dry-ground calcium carbonate particles having a median diameter in the range from 1.5 to 30.0 .mu.m in such an amount that the weight proportion of the precipitated calcium carbonate to the ground calcium carbonate is in the range from 20:80 to 80:20 and the solid concentration of the resulting aqueous slurry is in the range from 60 to 85% by weight;(c) subjecting the aqueous slurry of (b) to a secondary dispersing treatment by using a mixer so that the slurry has a viscosity not exceeding 1000 centipoise at 25.degree. C.; and(d) subjecting the aqueous slurry of (c) to a tertiary dispersing treatment in a sand grinding mill so that the median diameter of the calcium carbonate particles is in the range from 0.2 to 2.0 .mu.m.