초록

Novel processes are provided for the production of porous ceramic preforms, metal activated porous ceramic preforms and intermetallic/ceramic/metal composites. These products are all manufactured using processes which are based on tape casting techniques.

대표청구항 ▼

[ The embodiments in which an exclusive property or privilege are claimed are defined by the claims which now follow:] [1.] A process for preparing a ceramic preform having graded porosity and adapted for reactive metal infiltration processing which comprises:1) preparing tapes having controlled mic

[ The embodiments in which an exclusive property or privilege are claimed are defined by the claims which now follow:] [1.] A process for preparing a ceramic preform having graded porosity and adapted for reactive metal infiltration processing which comprises:1) preparing tapes having controlled microporosities by:a) preparing various colloidal suspensions formed from a ceramic powder, having a particle size in the range of about 0.2 to 2.0 microns, in admixture with a binder, a dispersant, a plasticizer, a solvent and at least one pyrolysable pore forming agent;b) casting said colloidal suspensions into discrete thin sheets; andc) drying said sheets to thereby form tapes having preselected pliability properties and microporosities, said microporosities being determined by adding varying amounts and/or particle sizes of pore forming agents to the differing colloidal suspensions, to thereby form tapes having differing porosities;2) preparing tapes having controlled microporosities and having varying quantities of metal activator embedded therein by:a) preparing various colloidal suspensions formed from a ceramic powder, having a particle size in the range of about 0.2 to 2.0 microns, in admixture with a binder, a dispersant, a plasticizer, a solvent, at least one pyrolysable pore forming agent and a particulate metal activator;b) casting said colloidal suspensions into discrete thin sheets;c) drying said sheets to thereby form tapes having preselected pliability properties and porosities, said porosities being determined by varying the quantity and particle size of the added pore forming agent, and having preselected amounts of dispersed metal activator embedded therein said metal activator being present in differing quantities thereby forming tapes having differing metal activator content;3) cutting shaped pieces of the tapes formed by steps (1) and (2);4) selectively layering a predetermined number of said tape pieces, in varying combinations, within a forming member, and compacting said layers at pressures ranging from between about 10 to 60 MPa, at temperatures ranging from between about 25.degree. C. to 75.degree. C. for a time ranging from between about 0.5 to 5 minutes to laminate said tape components and form a green body;5) heating said green body at a controlled rate, at temperatures effective to remove the pyrolysable suspension additives and form a brown body;6) deoxidizing the brown body by heating it in a reducing atmosphere to thereby convert any formed metal oxides to the metal; and7) firing said brown body at temperatures effective to sinter the ceramic structure to a predetermined degree for a time in the range of about 0.5 to 3 hours to thereby form the porous ceramic preform having controlled, and graded microporosity and having a metal activator embedded therein.