초록 ▼

Linear low density copolymer of ethylene/1-hexene is made processible into heat shrinkable film by a continuous process starting with the extrusion of the copolymer as a film. The production rate of heat shrinkable film made from linear low density copolymer of ethylene/1-octene-can be increased by

Linear low density copolymer of ethylene/1-hexene is made processible into heat shrinkable film by a continuous process starting with the extrusion of the copolymer as a film. The production rate of heat shrinkable film made from linear low density copolymer of ethylene/1-octene-can be increased by the step of blending a minor proportion of highly branched low density polyethylene with either copolymer prior to extrusion.

대표청구항 ▼

[ What is claimed is:] [1.] In an improved process for manufacturing satisfactorily drawn heat shrinkable films, which process comprising the steps of:a) blending:i) about 50 to 95 percent by weight of a single melting point, linear low density ethylene copolymer (LLDPE) having a density from about

[ What is claimed is:] [1.] In an improved process for manufacturing satisfactorily drawn heat shrinkable films, which process comprising the steps of:a) blending:i) about 50 to 95 percent by weight of a single melting point, linear low density ethylene copolymer (LLDPE) having a density from about 0.900 to about 0.935 g/cc, andii) about 5 to 50 percent by weight of a branched low density polyethylene LDPE having a density in the range of about 0.920 to about 0.925 g/cc and a branch structure produced by high pressure polymerization using a free radical initiator,b) extruding the blend through a die to make a tubular sheet or film at an extrusion temperature greater than about 215.degree. C., andc) heating the tubular sheet or film to its orientation temperature range, andd) substantially uniformly stretching the tubular sheet or film to accomplish orientation; improvement which comprises:accomplishing said stretching by expanding said tubular sheet or film to form a bubble and advancing the expanded tube of the film at a faster rate than the extrusion rate, to obtain a stretch of at least 3.5.times. in the machine direction and at least 3.times. in the transverse direction.