초록 ▼

A process and associated apparatus used to prepare a thermoplastic composite from a plurality of plies of thermoplastic resin prepregs. The prepregs are formed into a composite structure under two chambers; a rigid outer chamber (of any convenient size or shape) and a second flexible inner chamber c

A process and associated apparatus used to prepare a thermoplastic composite from a plurality of plies of thermoplastic resin prepregs. The prepregs are formed into a composite structure under two chambers; a rigid outer chamber (of any convenient size or shape) and a second flexible inner chamber containing a prepreg lay-up. The absolute pressures are reduced concurrently in a stepwise method in both chambers. This concurrent, stepped pressure reduction is accomplished at a rate which prevents the vacuum bag from moving far from the prepregs, and prevents wrinkles from forming in the prepregs. Pinching off the diffusion paths required for the removal of unwanted gases is eliminated. The lay-up is then heated and the absolute pressure in the outer rigid chamber is increased. This pressure constrains the flexible inner chamber during out-gassing of the thermoplastic resin, preventing wrinkles from forming in the prepregs. The absolute pressure in the outer rigid chamber is increased to atmospheric pressure or greater causing the prepregs to consolidate. A low absolute pressure is maintained in the flexible inner chamber. The temperature is then increased to the cure temperature of the resin and held for a time sufficient for the resin to cure. The resulting consolidated thermoplastic resin is substantially void free and detectable wrinkles are absent.

대표청구항 ▼

[ I claim:] [1.] A process of making a substantially void-free and wrinkle-free consolidated thermoplastic-resin composite having a low void content from a plurality of prepregs impregnated with a thermoplastic resin placed on a flat or contour shaped base or mold contained in a flexible inner chamb

[ I claim:] [1.] A process of making a substantially void-free and wrinkle-free consolidated thermoplastic-resin composite having a low void content from a plurality of prepregs impregnated with a thermoplastic resin placed on a flat or contour shaped base or mold contained in a flexible inner chamber having an absolute pressure, said inner chamber surrounded by an outer chamber having an absolute pressure, the process comprising the steps of:(a) reducing the absolute pressure in the flexible inner chamber and the absolute pressure in the outer chamber in increments in alternating unison to about 2 mm Hg while maintaining essentially equal pressures in both the flexible inner chamber and the outer chamber; then(b) heating the plurality of prepregs to a first temperature sufficient to lower the viscosity of the thermoplastic resin; then(c) increasing the absolute pressure in the outer chamber by about 20 mm Hg to 50 mm Hg; then(d) maintaining the absolute pressure in the flexible inner chamber at said about 2 mm Hg and the plurality of prepregs at said first temperature until removal of substantially all gases, water vapor, and volatiles from the plurality of prepregs; then(e) heating said plurality of prepregs to temperatures above the melting point of the thermoplastic resin while maintaining the absolute pressure in the inner chamber at said about 2 mm Hg and said absolute pressure in said outer chamber at said about 20 mm Hg to 50 mm Hg; then(f) increasing the absolute pressure in said outer chamber to at least atmospheric pressure at a controlled rate causing an increase of pressure on said flexible inner chamber thereby causing an increased pressure on the plurality of prepregs by the flexible inner chamber while maintaining said absolute pressure of said inner chamber at said about 2 mm Hg and at said temperatures above the melting point of the thermoplastic resin for a time sufficient to consolidate the plurality of prepregs together due to the increased pressure of the flexible inner chamber on the plurality of prepregs, and then(g) lowering the temperature of said plurality of prepregs to ambient temperature and venting said flexible inner chamber and said outer chamber to atmospheric pressure to obtain said substantially void-free and wrinkle-fee consolidated thermoplastic-resin composite.