초록 ▼

A cordierite body is produced by providing cordierite-forming raw materials. The raw materials are intimately blended with effective amount of vehicle and forming aids to impart plastic formability and green strength to the raw materials and form a plastic mixture. A green body is formed which is dr

A cordierite body is produced by providing cordierite-forming raw materials. The raw materials are intimately blended with effective amount of vehicle and forming aids to impart plastic formability and green strength to the raw materials and form a plastic mixture. A green body is formed which is dried and heated from room temperature up to a maximum temperature of about 1360.degree. C. to 1435.degree. C. at an average heating rate of at least about 315.degree. C. per hour and held at maximum temperature for about 0.05 to 4.4 hours. The total heating time from room temperature to the end of the hold at the maximum temperature is less than about 4.5 hours. The resulting body is predominately cordierite, having a mean coefficient of thermal expansion from about 25.degree. C. to 800.degree. C. of less than about 15.times.10.sup.-7.degree. C..sup.-1 in at least one direction. In another embodiment, the raw materials are talc, an alumina-forming source, and silica, wherein the mean particle diameter of the talc is less than about 4 micrometers, and that of the alumina--forming source is less than about 2 micrometers.

대표청구항 ▼

[What is claimed is:] [1.]a) combining talc, an alumina-forming source, and silica raw materials, wherein the mean particle diameter of the talc is less than about 4 micrometers, and the mean particle diameter of the alumina-forming source is less than about 2 micrometers;b) intimately blending the

[What is claimed is:] [1.]a) combining talc, an alumina-forming source, and silica raw materials, wherein the mean particle diameter of the talc is less than about 4 micrometers, and the mean particle diameter of the alumina-forming source is less than about 2 micrometers;b) intimately blending the raw materials with an effective amount of vehicle and forming aids to impart plastic formability and green strength to the raw materials and form a plastic mixture therefrom;c) forming said plastic mixture into a green body;d) drying the green body; ande) heating said green body from room temperature up to a maximum temperature of about 1360.degree. C. to 1435.degree. C. at an average heating rate of at least about 315.degree. C. per hour and holding at said maximum temperature for about 0.05 hours to 4.4 hours, wherein the total heating time from room temperature to the end of the hold at the maximum temperature is no greater than about 4.5 hours, to produce a body that is predominately cordierite, having a mean coefficient of thermal expansion from about 25.degree. C. to 800.degree. C. of less than about 15.times.10.sup.-7.degree. C..sup.-1 in at least one direction.